Mo-Si材料相组成与热膨胀性能的研究 预览 被引量:2

Phase Composition and Coefficient of Thermal Expansion of Mo-Si Composites Prepared by Liquid Reactive Sintering
在线阅读 下载PDF
收藏 分享 导出
摘要 利用液相反应烧结制备不同配比的Mo-S i复合材料,用X射线分析相组成,扫描电镜观察微观组织形貌,热膨胀仪测不同块体材料的热膨胀系数(CTE)。研究结果表明,不同配比烧结体相组成以MoS i2为主,当S i/Mo为2.2∶1(at%)时MoS i2基体中仍含有极少量的Mo5S i3相,而S i/Mo为2.3∶1时生成纯MoS i2。复合材料的CTE随Mo5S i3相含量的减少而增加,当S i/Mo达到2.3∶1时,CTE为最大值(8.16×10-6K-1)。 The composites of different Mo/Si ratio were prepared by vacuum liquid reactive sintering.The phase composition and microstructure of composites was analyzed by XRD and SEM,respectively.Their coefficients of thermal expansion(CTE) were measured by thermal dilatometer.MoSi_2 was primary phase in the composites.There was a little Mo_5Si_3 phase in the composite when Si/Mo ratio was 2.2∶1.With Si/Mo ratio increase to 2.3∶1 Mo_5Si_3 phase disappeared.The CTE increased with content of Mo_5Si_3 phase decreasing a...
作者 肖来荣 蔡志刚 易丹青 刘瑞 XIAO Lai-rong; CAI Zhi-gang; YI Dan-qing; LIU Rui(College of Material Science and Engineering; Central South University; Changsha 410083; China);
出处 《航空材料学报》 EI CAS CSCD 2006年第4期,共5页 Journal of Aeronautical Materials
关键词 液相反应烧结 Mo-Si复合材料 热膨胀系数 liquid reactive sintering Mo-Si composite coefficients of thermal expansion
  • 相关文献

参考文献16

  • 1马勤,杨延清.二硅化钼—用途广泛的金属间化合物[J].材料开发与应用,1997,12(6):27-32. 被引量:8
  • 2[2]VASUDEVAN A K,PETROVIC J.Comparative overview of molybdenum disilicide composites[J].Journal of Material Science,1990,25:4453-4456. 被引量:1
  • 3[3]PERIO A.Growth of MoSi2 with preferential orientation on(100) silicon[J].Application Physics Letter,1984,45(8):857-859. 被引量:1
  • 4肖来荣,易丹青,殷磊,李洪武.铌及铌合金高温涂层研究进展[J].材料导报,2004,18(1):13-15. 被引量:18
  • 5[6]《难熔金属论文集》编辑组.难熔金属及其合金的防护涂层[M].上海:上海科学技术情报研究所,1974. 被引量:1
  • 6[7]JIN-KOOK YOON,GYEUNG-HO KIM.Simultaneous growth mechanism of intermediate silicides in MoSi2/Mo system[J].Surface and Coatings Technology,2001,148:129-135. 被引量:1
  • 7[8]MITRA R,MAHAJAN Y R.Processing-microstructureproperty relationships in reaction hot-pressed MoSi2 and MoSi2/SiCp composites[J].Mater Sci & Eng,1997,A225:105-117. 被引量:1
  • 8[9]DEEVI S C,THADHANI N N.Reaction synthesis of hightemp.silicides[J].Materials Science and Engineering,1995,A192/193:604-611. 被引量:1
  • 9[10]JO S W,LEE G W,Kim Y S.On the formation of MoSi2 by self-propagating high-temp[J].Synthesis Acta Mater,1996,44(11):4317 -4326. 被引量:1
  • 10来忠红,朱景川,王丽艳,尹钟大.原位复合Mo-Si化合物材料的相组成和力学性能[J].材料科学与工艺,2003,11(3):248-250. 被引量:3

二级参考文献35

共引文献26

同被引文献30

引证文献2

二级引证文献3

投稿分析

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部 意见反馈