电磁场对电弧熔积快速成形温度场及残余应力的影响 预览 被引量:4

Influence of electromagnetic field on temperature field and residual stress in arc deposition rapid prototyping
在线阅读 下载PDF
收藏 分享 导出
摘要 为了研究在电孤熔积快速成形过程中附加电磁场之后成形工件表面温度场发生的改变,以及温度场变化对成形件造成的影响,使用红外热像仪对附加电磁场前后的电弧熔积成形过程进行了实时拍摄,并用X射线衍射测应力法对得到的成形件表面残余应力进行了测量.结果表明,附加磁场后,成形件表面温度场各温度区域尺寸扩大,熔积层表面所经历的最高温度升高,冷却速度减缓,成形件表面的纵向及横向残余应力均减小. In order to study the change of surface temperature field and its influence on forming part of arc deposition manufacturing process with additional electromagnetic fields,the real time image during arc deposition manufacturing with additional electromagnetic field and without it were acquired by infrared thermal imager respectively,and the surface residual stress of forming part was measured by using X-ray diffraction stress text.The results showed that the size of each temperature region of surface temperature field had expended,the highest temperature of deposition layer had increased and the cooling rate had been slowed down,longitudinal and transverse residual stresses of surface had reduced.
作者 王桂兰 孙怡峰 柏兴旺 张海鸥 WANG Gui-lan 1,SUN Yi-feng 1,BAI Xing-wang 2,ZHANG Hai-ou 2(1.State Key Laboratory of Materials Processing and Die & Mould Technology,Huazhong University of Science & Technology,Wuhan 430074,Hubei pro.,China;2.State Key Laboratory of Digital Manufacturing Equipment & Technology,Huazhong University of Science & Technology,Wuhan 430074,Hubei pro.,China)
出处 《焊接技术》 北大核心 2013年第3期共3页 Welding Technology
基金 航空科学基金
关键词 电弧熔积快速成形 电磁场 温度场 残余应力 arc deposition rapid prototyping,electromagnetic field,temperature field,residual stress
  • 相关文献

参考文献7

  • 1张海鸥;王超;胡帮友.金属零件直接快速制造技术及发展趋势,2010(08). 被引量:1
  • 2王桂兰;杨磊;张海鸥.金属熔积直接成形翘曲变形的有限元分析,2012(08). 被引量:1
  • 3阿勃拉洛夫M A;阿勃拉杜赫曼诺夫PY.电磁作用焊接技术,1988. 被引量:1
  • 4张忠典;李冬青.外加磁场对焊接过程的影响,2002(03). 被引量:1
  • 5Sadek C A Alfaro;Fernand Diaz Franco.Exploring infrared sensoring for real time welding defects monitoring in GTAW,2010. 被引量:1
  • 6杨立.红外热像仪测温计算与误差分析,1999(04). 被引量:1
  • 7常云龙;车小平.外加磁场对MIG焊熔滴过度形式和焊缝组织性能的影响,2008(10). 被引量:1

同被引文献50

引证文献4

二级引证文献4

投稿分析

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部 意见反馈