氧化钆掺杂二氧化钛催化超声降解甲基橙的研究 预览 被引量:21

Study on Ultrasonic Degradation of Methyl Orange on Gd2O3-doped TiO2 Catalyst
在线阅读 下载PDF
收藏 分享 导出
摘要 用实验室合成的Gd2O3掺杂TiO2为催化剂,以甲基橙超声降解反应为模型,研究了各种因素对Gd2O3掺杂TiO2催化超声降解甲基橙的影响.研究结果表明,Gd2O3掺杂TiO2催化超声降解甲基橙的效果明显优于非掺杂的锐钛矿型TiO2的情况;在甲基橙溶液pH 1.0~3.0、甲基橙质量浓度20 mg/L、溶液用量100 mL、催化剂用量0.5~1.0 g/L的条件下,用输出功率1.0 W/cm2和频率25 kHz的超声波照射60 min,甲基橙降解率可达98.6%,COD去除率可达99.0%. The various affecting factors were studied on ultrasonic degradation of methyl orange in the presence of Gd_2O_3-doped TiO_2 catalyst prepared in laboratory.The results indicate that the effects of ultrasonic degradation are more obvious in the presence of Gd_2O_3-doped TiO_2 catalyst than in the presence of pure anatase TiO_2 catalyst.Under the conditions of solution pH 1.0-3.0,methyl orange mass concentration 20 mg/L,solution volume 100 mL,catalyst dosage 0.5-1.0 g/L,irradiation power 1.0 W/cm~2,frequency 25 kHz,and irradiation time 60 min,the degradation rate of methyl orange can come up to 98.6% and the removal rate of COD to 99%.
作者 王君 韩建涛 张向东 刘振荣 郭宝东 佟键 张鹏 康平利 Wang Jun~1,Han Jiantao~1,Zhang Xiangdong~1,Liu Zhenrong~1,Guo Baodong~1, Tong Jian~2,Zhang Peng~2,Kang Pingli~2 (1.Department of Chemistry,Liaoning University,Liaoning Shenyang 110036,China; 2.Center of Analysis and Test,Liaoning University,Liaoning Shenyang 110036,China)
出处 《化工环保》 CAS CSCD 北大核心 2004年第3期 161-164,共4页 Environmental Protection of Chemical Industry
基金 国家自然科学基金
关键词 氧化钆掺杂 二氧化钛 催化剂 超声降解 甲基橙 gadolinium sesquioxide doping titanium dioxide catalyst ultrasonic degradation methyl orange
  • 相关文献

参考文献17

二级参考文献80

共引文献433

同被引文献285

引证文献21

二级引证文献101

投稿分析

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部 意见反馈
新型冠状病毒肺炎防控与诊疗专栏