超支化聚酯改性超细氧化锌 预览 被引量:2

Modification of Ultrafine ZnO Particles by Hyperbranched Polyester
在线阅读 下载PDF
收藏 分享 导出
摘要 采用富含-COOH基团的超支化聚酯(HBP)对超细氧化锌(μ-ZnO)进行表面改性,并对改性后的氧化锌的结构和特征进行了表征.结果表明:在氨水中得到了稳定期较长、清澈透明的μ-ZnO悬浮液,在n(-COOH)/n(μ-ZnO)为1/8时稳定期最长,超过72 h;采用相同的方法,但溶剂为丙酮或乙酸丁酯时,稳定期只有0.5~1 h;改性后的μ-ZnO在1 575 cm-1处出现新的振动吸收,表面包覆了聚合物,团聚现象不明显,分散状态得到明显的改善. Nano-meter and micro scale zinc oxide particles were modified by hyperbranched polyesters (HBP) containing COOH groups, and the structure and characterisrics of the surface modified ZnO particles were characterizedThe results showed stable transparent suspension solutions of ZnO in ammonia aqueous were prepared by the addition of HBP When COOH/ZnO=1/8, the time of maintaining suspension solutions transparent was over 72 h On the contrast, the time was only 05~1 h when changing to acetone or butane acetate as the solventsIn the IR spectra, new vibration absorption appeared at 1575 cm -1XPS,elemental analyses and TEM data indicated that the HBP was bonded onto the surface of ZnO powders, and the aggregating of ZnO powders was depressed
作者 朱振东 罗凯 苏琳 王跃川 ZHU Zhen-dong, LUO Kai, SU Lin, WANG Yue-chuan (The State Key Lab for Polymer Materials Eng, College of Polymer Sci and Eng, Sichuan University, Chengdu 610065, China)
出处 《塑料工业》 CAS CSCD 北大核心 2005年第2期 51-53,64,共4页 China Plastics Industry
关键词 超支化聚酯 超细氧化锌 表面改性 氨水 稳定期 Hyperbranched Polyester Ultrafine ZnO Surface Modification Ammonia Aqueous Stability Time
  • 相关文献

参考文献18

二级参考文献4

共引文献108

同被引文献28

  • 1陈庆华,肖荔人,辛晓晶,钱庆荣,郑德.可环境消纳塑料助剂——稀土类光敏剂的研究与应用[J].塑料,2004,33(4):19-24. 被引量:6
  • 2姚超 ,丁永红 ,林西平 ,杨绪杰 ,陆路德 ,汪信 .纳米TiO2有机表面改性的研究[J].无机化学学报,2005,21(5):638-642. 被引量:45
  • 3何晓囡 ,李文军 ,徐瑞芬 ,侯国平 .超分散剂对纳米TiO2的表面改性研究[J].化工新型材料,2005,33(8):47-49. 被引量:11
  • 4王国建,屈泽华,李岩,刘琳.超支化聚酯修饰多壁碳纳米管[J].应用化学,2007,24(7):828-831. 被引量:10
  • 5KIM Y H, WEBSTER O. Hyperbranched polymers [ J ]. Polymer Reviews, 2002 ,42 ( 1 ) :55 -89. 被引量:1
  • 6HIDEHARU M, DELPHINE C S, ZHANG M F, et al. Hybrid nanopartical with hyperbranched polymer shells via self - condensing atom transfer radical polymerization from silica surfaces [ J ]. Langmuir, 2002, 18:3 682 -3 693. 被引量:1
  • 7TSUKRUK V V. Dendritic macromolecules at interfaces[ J]. Advanced Materials, 1998 (10) :253 - 257. 被引量:1
  • 8BOSMAN A W, JANNSEN H M, MEIJER E W. About dendrimers: structure, physical properties, and applicationa[ J]. Chemical Reviews, 1999, 99:1 665-1 688. 被引量:1
  • 9TSUBOKAWA N, HAYASHI S, NISHIMURA J. Grafting of hyperbranched polymers onto ultrafine silica: postgraft polymerization of vinyl monomers initiated by pendant azo groups of grafted polymer chains on the surface[ J]. Progress in Organic Coatings, 2002, 44: 69 - 74. 被引量:1
  • 10TANIGUCHI Y, OGAWA M, WEI G, et al. Preparation of hyperfunctinal carbon black by grafting of hyperbranched polyester onto the surface[ J]. Materials Chemistry and Physics, 2008, 108:397 - 402. 被引量:1

引证文献2

二级引证文献3

投稿分析

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部 意见反馈