等离子弧焊直接金属成形技术的工艺研究 预览 被引量:8

Process Reasearch for Direct Metal Forming Based on Plasma Arc Welding
在线阅读 免费下载
收藏 分享 导出
摘要 提出了一种基于等离子弧焊的直接金属成形新方法,通过对成形工艺的试验研究,确定了焊接电流、成形速度与成形轨迹宽度之间的对应关系;针对成形轮廓的表面质量问题,实施了根据轮廓矢量进行切向送丝的填充方案;并采用循环水冷的温控措施解决了成形过程的过热问题. Direct metal forming based on plasma arc welding is a novel rapid prototyping process. Relationship among welding bead width, welding current and speed was obtained through process experiments. Furthermore, an adaptive wire feeding manner which can adjust the feeding direction relative to the track tangent is introduced to improve the bead quality. A water cooling method was also developed to control the heat accumulation during forming.
作者 胡晓冬 赵万华 HU Xiao-dong 1 , ZHAO Wan-hua 2 (1Zhejiang University of Technology, Hangzhou 310014; 2 Xi′an Jiaotong University, Xi′an 710049)
出处 《机械科学与技术》 CSCD 北大核心 2005年第5期 540-542,共3页 Mechanical Science and Technology
基金 全国高等学校优秀博士学位论文作者专项基金
关键词 快速成形 直接金属成形 弧焊 Rapid prototyping Direct metal forming Arc welding
  • 相关文献

参考文献3

  • 1Segal F I, Campbell R I. A review of research into the effects of rapid tooling on part properties [J]. Rapid Prototyping Journal, 2001, 7(2): 90-98. 被引量:1
  • 2Cooper K G, Rapid Prototyping Technology: Selection and Application [M]. Marcel Dekker Inc. , New York, 2001. 被引量:1
  • 3胡晓冬..基于弧焊的直接金属成形技术研究 [D].西安交通大学,2003:

同被引文献106

引证文献8

二级引证文献28

投稿分析

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部 意见反馈