Pt—Al涂层的高温氧化行为 预览 被引量:5

High Temperature Oxidation Behaviour of Platinum-modified Aluminide Coating
在线阅读 下载PDF
收藏 分享 导出
摘要 在M38G高温合金上镀铂,然后进行粉末包装渗铝,最后形成Pt-Al涂层,经1000℃,1500h氧化后,发现涂层中加铂,明显改善氧化膜的粘附性和影响铝的扩散,并讨论铂在氧化中的作用机理。 The platinum-modified aluminide coating was prepared by elec-troplating platinum and then pack cementation of aluminum on M38G supperalloy.The oxidation behaviour of coating was studied at 1000℃ for 1500 hours.The oxidized samples were analysed by optical microscope,EMPA and X-ray diffraction techniques.The results clearly indicate that the addition of platinum can remarkably enhance the adhesion of the oxide scales and affect the diffusion of aluminum in the coating.The mechani-sms of the effect of platinum on the oxidation were discussed.
作者 白林祥 Bai Linxiang and Wu Weitao(Institute of Corrosion and Protection of Metals,Academia Sinica,Shenyang 110015)
出处 《贵金属》 CAS CSCD 北大核心 1995年第1期 24-29,共6页 Precious Metals
关键词 涂层 高温氧化 腐蚀试验 Platinum,Aluminum,Coating, High-temperature oxidation test
  • 相关文献

参考文献1

  • 1白林祥,楼翰一,吴维(山文).铂改进铝化物涂层的组织和抗热腐蚀性能[J]材料保护,1988(01). 被引量:1

同被引文献132

引证文献5

二级引证文献45

投稿分析

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部 意见反馈