磁热锰锌铁氧体湿法制备工艺研究 预览

Research on Preparation of the Thermomagnetic Mn-Zn Ferrite
在线阅读 下载PDF
收藏 分享 导出
摘要 用化学共沉淀法研制了磁热锰锌铁氧体,并对样品进行了前驱体颗粒度测试,磁滞回线、X-射线衍射及发热实验测定.结果表明,共沉淀工艺的最佳pH值为4,最佳保温温度为70℃,保温时间为1.5h.加料采用逆加法和滴加法.最佳烧结温度是800℃.在交变磁场下,有明显的磁热效应.与干法比,湿法所得锰锌铁氧体性能更好. The Mn-Zn ferrite of thermomagnetic effect was prepared by coprecipitation. The samples were tested by LS Particle Size Analyzer for precursor, and the hysteresis loop, XRD and thermomagnetic tests were also carried out. The results show that the best pH value is 4, the best preserved temperature is 70℃ and the best preserved time is 1.5h. We use reversal drop-method to add reagent. Being placed under alternative magnetic field, the samples have the obvious thermomagnetic effect. Compared to dry preparation, the Mn-Zn ferrite prepared by wet preparation has better quality.
作者 唐小亮 吴知方 李培荣 黄文旵 Tang XiaoLiang;Wu ZhiFang;Li PeiRong;Huang Wen旵
出处 《玻璃与搪瓷》 CAS 2005年第4期 19-23,10,共6页 Glass & Enamel
基金 国家自然科学基金,上海市纳米科技专项基金
关键词 共沉淀法 铁氧体 磁滞回线 磁热效应 coprecipitation ferrite hysteresis loop thermomagnetic effect
  • 相关文献

参考文献7

二级参考文献21

  • 1邓尚斌.磁性材料及器件,1996,27(1):50-50. 被引量:1
  • 2Yong S Cho, et al. Homogeneous grain growth and fast-firing of chemically modified nanocrysta- lline MnZn ferrite, 1999, 34(14/15): 2361-2368. 被引量:1
  • 3Yong S.Cho, et al. J Am Ceram Soc, 1999, 82(6): 1416-1420. 被引量:1
  • 4Komarneni S, et al. J Am Ceram Soc, 1988, 71(1): c-26--c-28. 被引量:1
  • 5Rozman M, et al. J Am Ceram Soc, 1995, 78(9) : 2449-2455. 被引量:1
  • 6Znidarsic A, et al. J Am Ceram Soc, 1999, 82(2): 359-365. 被引量:1
  • 7Shi J L, et al. J Euro Ceram Soc 1994,13: 265-273. 被引量:1
  • 8Rozman M, et al. J Am Ceram Soc, 1998, 81(7): 1757-1764. 被引量:1
  • 9Zhu M Y, et al. J Am Ceram Soc. 1991, 74(6): 1217-1225. 被引量:1
  • 10Tanaka T. J Am Cerara Soc, 1981, 64(7): 419-421. 被引量:1

共引文献49

投稿分析

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部 意见反馈
新型冠状病毒肺炎防控与诊疗专栏