5083铝合金热压缩变形流变应力行为 预览 被引量:31

Flow stress behavior of 5083 aluminium alloy under hot compression deformation
在线阅读 下载PDF
收藏 分享 导出
摘要 在Gleeble-1500热模拟机上,当变形温度为300-500℃、应变速率为0.01-10 s^-1、真应变为0-0.8时,采用圆柱体等温热压缩实验研究5083铝合金变形流变应力行为。通过分析流变应力指数函数中系数A、β与应变的关系,建立Zener-Hollomon参数的指数关系本构方程。运用该本构方程对5083铝合金不同应变速率、变形温度及应变条件下的流变应力进行预测,发现流变应力预测值与温升修正值吻合得相当好。 The flow stress behavior of 5083 aluminium alloy under hot compression deformation, in the temperature range of 300-500 ℃, strain rates of 0.01-10 s ^-1 and true strains of 0-0.8, was investigated by cylindrical compression tests on Gleeble 1 500 machine. The constitutive equations were presented considering the values of A and β as function of strain by Zener-Hollomon parameter in the exponential function form. Using the constitutive equations presented, the prediction of the flow stress in 5083 aluminium alloy as function of strain rate, temperature and strain shows to be in good agreement with the measured flow stresses corrected for temperature rise.
作者 吴文祥 孙德勤 曹春艳 王战锋 张辉 WU Wen-xiang, SUN De-qing, CAO Chun-yan, WANG Zhan-feng, ZHANG Hui (1. Suzhou Institute for Non-ferrous Metals Processing Technology, Suzhou 215026, China; 2. School of Materials Science and Engineering, Hunan University, Changsha 410082, China)
出处 《中国有色金属学报》 EI CAS CSCD 北大核心 2007年第10期 1667-1671,共5页 The Chinese Journal of Nonferrous Metals
基金 中国铝业公司科技发展基金资助项目(2006KJA08)
关键词 5083铝合金 热压缩变形 温升 流变应力 本构方程 5083 aluminium alloy hot compression deformation temperature rise flow stress constitutive equations
作者简介 通讯作者:吴文祥;电话:0512-88856525;E-mail:wwx985@163.com
  • 相关文献

参考文献15

二级参考文献55

共引文献168

同被引文献325

引证文献31

二级引证文献90

投稿分析

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部 意见反馈