不锈钢相变的研究进展 预览 被引量:4

Research Progress of Phase Transformation of Stainless Steel
在线阅读 下载PDF
收藏 分享 导出
摘要 综述了各类不锈钢相变的研究进展以及主要合金元素对相变的影响。铁素体不锈钢高温加热时,有碳化物和氮化物析出,降低耐蚀性、韧性;马氏体不锈钢加热过程中发生马氏体向奥氏体的转变;奥氏体不锈钢加热到1300℃以上时,发生高温δ相变,产生高温铁素体,冷却或经受冷变形时,发生马氏体相变,相变产物为δ和α'组织;双相不锈钢中由于奥氏体的存在,相变与奥氏体不锈钢相似。 The research progress of phase transformation of stainless steel was summarized, the effects of main alloy elements on phase transformation were also discussed. In ferrite stainless steel, carbide and nitride will be precipitated when heating to high temperature, which reduces corrosion resistance and toughness. The M(martensite)→γ (anstenite) transformation occurs during heating in martensite stainless steel. The γ(austenite)→δ(ferrite ) transformation occurs when heating above 1300 ℃ in austenite stainless steel, martensite transformation occurs when cooling or undergoing cold-work. As a result of austenite existing, the phase transformation in duplex stainless steel is similar to that in austenite stainless steel.
作者 徐建林 居春艳 季根顺 XU Jianlin, JU Chunyan, JI Genshun(1.State Key Laboratory of Gansu Advanced Nonferrous Metal Materials, Lanzhou University of Technology, Lanzhou 730050, China; 2. Key Laboratory of Non-ferrous Metal Alloys, The Ministry of Education, Lanzhou University of Technology, Lanzhou 730050, China)
出处 《热加工工艺》 CSCD 北大核心 2008年第14期 104-107,共4页 Hot Working Technology
关键词 不锈钢 相变 进展 stainless steel phase transformation progress
作者简介 徐建林(1970-),男,陕西岐山人,副教授,博士,主要从事材料科学与计算机应用的研究;电话:0931-3316414;E—mail:ggdjlxu@sina.com
  • 相关文献

参考文献18

二级参考文献70

共引文献126

同被引文献70

引证文献4

二级引证文献15

投稿分析

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部 意见反馈
新型冠状病毒肺炎防控与诊疗专栏