WO3对掺铒碲酸盐玻璃光谱性质的影响 被引量:2

Effects of WO3 on optical properties of Er^3+ -doped tungsten-tellurite glasses
分享 导出
摘要 制备了掺铒碲钨酸盐玻璃(80-x)TeO2-(10+x)WO3-8BaO-2Na2O-0.5Er2O3(x=0,5,10,15,20)玻璃,研究了WO3对掺铒碲钨酸盐玻璃的光谱性质.研究发现:随着WO3含量的增加,Ω4,Ω6先增加后减小,受激发射截面也是先增加后减小,而Ω2的变化则相反.由McCumber理论计算了掺铒碲钨酸盐玻璃在1.5μm的受激发射截面,其最大受激发射截面为0.96×10^-21cm^2,Er^3+的^4Ⅰ13/2→^4Ⅰ15/2的跃迁发射荧光光谱的最大荧光半高宽为82 nm.同时,实验发现,在976 nm抽运下,掺铒碲酸盐玻璃存在较强的荧光上转换现象,随WO3含量的增加,上转换荧光强度呈降低的趋势. Tungsten-tellurite glasses with the molar compositions of (60 + x )TEO2-(30- x )WO3-8BaO-2Na2O-0.5Er2O3 (x = 0,5, 10, 15, 20) have been prepared. Effects of WO3 on optical properties of Er^3+ -doped tungsten-tellurite glasses have been discussed. Along with the WO3 content increasing, Ω2 and Ω6 first increase and then decrease, and the stimulated emission cross-section also behaves in like manner, while Ω4 changes contrarily. According to the McCumber theory, the maximum peak of σe is calculate to be 1.00×10^-21 cm^2 at 1.55 μm. The maximum FWHM of Er^3+ ^4Ⅰ13/2→^4Ⅰ15/2 emission spectrum is 82 nm. In addition, the intensity of upconversion luminescence of the Er^3+ -doped tungsten-tellurite glasses decreases rapidly with the increasing of WO3 content.
作者 贾相华 吕树臣 孙江亭 彭鸿雁 张梅恒 Jia Xiang-Hua, Lü Shu-Chen, Sun Jiang-Ting, Peng Hong-Yan, Zhang Mei-Heng (1 Mudanjiang Teachers College, Key Laboratory of Superhard Materials, Mudanjiang 157012, China; 2Department of Physics, Harbin Normal University, Harbin 150080, China)
出处 《物理学报》 SCIE EI CAS CSCD 北大核心 2008年第9期 5978-5982,共5页 Acta Physica Sinica
基金 超硬材料黑龙江省高校重点建设经费,凝聚态物理黑龙江省重点学科经费和实验室黑龙江省教育厅科学技术研究项目(批准号10541241)资助的课题.
关键词 碲钨酸盐玻璃 Er^3+光谱性质 Judd-Offelt理论 tungsten-tellurite glasses, Er^3+ spectroscopic properties, Judd-Ofeh theory
作者简介 通讯联系人E-mail:lushuchen63@yahoo.com.cn
  • 相关文献

参考文献20

二级参考文献68

共引文献11

同被引文献35

引证文献2

二级引证文献4

投稿分析

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部 意见反馈