大型齿轮圈铸钢件成型过程工艺优化 预览 被引量:9

Technological Optimization on Forming Process for Large Gear Ring Castings
在线阅读 下载PDF
分享 导出
摘要 利用华铸CAE软件对大型齿轮罔铸钢件进行了凝同过程南数值模拟,发现了缩孔、缩松缺陷,确定了其产生的位置,分析了其产生原因及机理。在此基础上对其铸造工艺进行了修改,工艺优化,又一次进行凝同模拟,对前后模拟结果进行了分析与比较。结果表明,合理设置保温冒口、冷铁的大小和位置,加上合适的冒口套,可以保证铸件顺序凝同和金属液的有效补缩,获得结构完整、没有缺陷的铸钢件。 Using Huazhu CAE software, the solidification process of large gear ring castings was simulated, the shrinkage was discovered, its position was defined, its cause and mechanism was analyzed. Based on this, the design of casting process was optimized, the solidification process was simulated again, the results of simulation were compared and analyzed. The results show that the reasonable size and placement of the insulated riser, iron chill and riser case can ensure castings progressive solidification and effective feeding of metal liquid, so the eligible castings with complete structure are obtained.
作者 庞富伟 王爱琴 谢敬佩 王文焱 PANG Fuwei, WANG Aiqin, XIE Jingpei, WANG Wenyan (College of Material Science and Engineering, He 'nan University of Science and Technology, Luoyang 471003, China)
出处 《热加工工艺》 CSCD 北大核心 2008年第19期 55-57,60,共4页 Hot Working Technology
基金 河南省杰出人才创新基金资助项目(0621000600)
关键词 齿轮罔 凝同模拟 缩孔 缩松 工艺优化 gear ring solidification simulation shrinkage technological optimization
作者简介 庞富伟(1982-),男,河南洛阳人,在读硕士研究生;主要研究方向:金属材料凝固过程及强韧化:电话:13721623763;E—mail:pfw2006@163.com
  • 相关文献

参考文献8

二级参考文献25

共引文献48

同被引文献103

引证文献9

二级引证文献60

投稿分析

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部 意见反馈