6082铝合金搅拌摩擦焊焊缝的电化学腐蚀行为 预览 被引量:12

Electrochemical corrosion behavior of friction stir welding weld of 6082 aluminum alloy
在线阅读 下载PDF
收藏 分享 导出
摘要 通过室温静态挂片试验以及动电位极化曲线测试,在室温0.2mol/LNaHSO3+0.6mol/L NaCl溶液中,对6082铝合金搅拌摩擦焊(FSW)焊缝以及6082铝合金母材的电化学腐蚀行为进行了研究。结果表明,主轴转速为1200r/min,焊接速度为200mm/min,搅拌头倾角为3°时的焊缝与母材相比,平均腐蚀速率较小,腐蚀电位Ecorr正向移动,腐蚀电流密度J变小。同时使用扫描电子显微镜(SEM)对室温静态挂片试验试样的表面形貌进行了观察,发现焊缝表面上只出现少量较浅的点蚀坑,而母材表面的点蚀现象较为严重。 In the ambient temperature solution of 0.2 mol/L NaHSO3 and 0.6 mol/L NaCl,the electrochemical corrosion behavior of friction stir welding weld of 6082 aluminum alloy and parent material were investigated by static weight loss experiment(gravimetric test) and potentiodynamic polarization curve.With the rotation rate of 1 200 r/min,the traverse speed of 200 mm/min and 3° tool tilt,the corrosion rate of the weld was less than that of the parent material,and the corrosion potential of the weld was more positive than that of the parent material,the corrosion current density was less than that of the parent material.SEM observation showed that a few shallow pits appeared on the surface of the weld,however,a large number of deeper pits emerged on the surface of the parent material.
作者 赵亚东 沈长斌 刘书华 葛继平 黄振晖 ZHAO Yadong1,SHEN Changbin1,LIU Shuhua1,GE Jiping1,Huang Zhenhui2(1.Liaoning Key Materials Laboratory for Railway,Dalian Jiaotong University,Dalian 116028,Liaoning,China;2.R&D Center,CNR Tangshan Railway Vehicle Limited Liability Company,Tangshan 063035,Hebei,China)
出处 《焊接学报》 EI CAS CSCD 北大核心 2008年第10期105-107,共3页 Transactions of The China Welding Institution
基金 大连市经委资助项目
关键词 铝合金 搅拌摩擦焊 焊缝 电化学腐蚀 aluminum alloy friction stir welding weld electrochemical corrosion
作者简介 赵亚东,男,1983年出生,硕士研究生。主要从事铝合金搅拌摩擦焊工艺研究。发表论文2篇。Email:shencb@djtu.edu.cn
  • 相关文献

参考文献7

  • 1Thomas W M, Nicholas E D, Needham J C. Friction stir welding: UK, PCT/GB92/02203[P]. 1991 - 10-06. 被引量:1
  • 2黄华,董仕节,刘静.先进的搅拌摩擦焊技术[J].有色金属,2006,58(1):60-63. 被引量:14
  • 3赵衍华,林三宝,申家杰,吴林.2014铝合金搅拌摩擦焊接头的微观组织及力学性能[J].航空材料学报,2006,26(1):67-70. 被引量:20
  • 4Ferrer K S, Kelly R G. Comparison of methods of removal of corrosion products from AA2024-T3[J]. Corrosion, 2001, 57(2): 110- 117. 被引量:1
  • 5Corral J, Trillo E A, Ying L, et al. Corrosion of friction-stir welded aluminum alloys 2024 and 2195[J]. Journal of Materials Science Letters, 2000, 19: 2117-2122. 被引量:1
  • 6Mishra R S, Ma Z Y. Friction stir welding and processing[ J]. Materials Science and Engineering R, 2005, 50( 1 - 2) : 1 - 78. 被引量:1
  • 7刘永辉,张佩芬编..金属腐蚀学原理[M].北京:航空工业出版社,1993:274.

二级参考文献51

  • 1赵家瑞,.一种焊接新工艺在迅速发展--搅拌摩擦焊[J].焊接技术,2000(z1):37-38. 被引量:7
  • 2Joelj D.The friction stir welding advantage [J].Welding journal,2001,80(5):30-34. 被引量:1
  • 3Thomas W M,Nicholas E D,Needham J C,et al.Friction stir butt welding.British:GB Patent Application,9125978.8[P].1991-09-06. 被引量:1
  • 4Dawes C J.An introduction to friction stir welding and its development [J].Welding & Metal Fabrication,1995,(1):12-16. 被引量:1
  • 5Thomas M W,Nicholas E D,Needham J C,et al.Friction stir welding.British:GB Patent Application,9125978[P].1991-12-08. 被引量:1
  • 6Rhodes C G,Mahoney M W.Effect of frication stir welding on micro structure of 7075 aluminum [J].Scripta Materialia,1997,36(1):69-75. 被引量:1
  • 7Dawes C J,Thomas W M.Friction stir process welds aluminum alloys [J].Welding journal (Miami,Pal),1996,75(3):41-45. 被引量:1
  • 8Thomas W M,Nicholas E D,Needham J C,et al.Temple-Smith P and Dawes CJ (TWI):Improvements relating to friction welding:European Patent,EP 0615 480 BI [P].1994-09-21. 被引量:1
  • 9Midling O T,Marley E J,Sandvik A.Frication stir welding:European Patent,EP 0752 926 BI [P].1997-01-15. 被引量:1
  • 10Waldron D J,Roberts R W.Friction stir welding--a revolutionary new joining method [ C]//Aerospace Automated Fastening Conference and Exposition.Long Beach,California,1998:15-17. 被引量:1

共引文献32

同被引文献117

引证文献12

二级引证文献47

投稿分析

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部 意见反馈