热处理对高压凝固Ti-48Al合金组织演变的影响 预览 被引量:2

Effect of heat treatment on microstructure evolution of Ti-48Al alloy solidified under high pressure
在线阅读 下载PDF
分享 导出
摘要 采用六面顶压机制备2和4 GPa下高压凝固试样,并在真空封装后进行1100℃保温12 h空冷的高温热处理实验,研究经高压凝固后Ti-48Al合金组织的演变规律以及高压凝固后热处理对Ti-48Al合金组织变化的影响。结果表明:经高压凝固后,随着凝固压力的增加,枝晶间γ相数量减少;当压力到达4 GPa时,片层组织的体积分数约为99.31%。经热处理后,常压凝固试样变化不大,而高压凝固试样中均形成魏氏组织,采用1100℃炉冷热处理和EBSD技术进行分析,确定了高压下魏氏体组织的形成机制。 High pressure solidification samples were prepared at 2 and 4 GPa on a HTDS-032F type cubic hydraulic pressure machine. Then, the samples were heat-treated at 1120℃ for 12 h. The effect of high pressure on the microstructure evolution of Ti-48Al alloy solidified under high pressure and heat treatment on the microstructure evolution of Ti-48Al alloy solidified under different pressures were investigated. The results indicate that, when solidified under high pressure, theγ-segregate phase decreases with increasing the pressure. When the pressure reaches 4 GPa, the volume fraction of lamellar structure is about 99.31%. After heat treatment, the microstructure solidified under normal pressure is not changed, but Widmanst-tten lamellar microstructure forms in high pressure solidified samples by NAKA mechanism, which is confirmed by heat treatment and EBSD analysis.
作者 朱冬冬 董多 倪成员 周兆忠 张德丰 魏尊杰 ZHU Dong-dong,DONG Duo,NI Cheng-yuan,ZHOU Zhao-zhong,ZHANG De-feng,WEI Zun-jie (1. School of Mechanical Engineering, Quzhou University, Quzhou 324000, China) (2. School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001, China)
出处 《中国有色金属学报》 EI CAS CSCD 北大核心 2015年第1期58-62,共5页 The Chinese Journal of Nonferrous Metals
基金 衢州学院校科研启动基金资助项目(BSYJ201407)浙江省教育厅科研项目(Y201431713)
关键词 钛铝金属间化合物 高压凝固 热处理 魏氏体 TiAl intermetallic high pressure solidification heat treatment Widmanst?tten
作者简介 通信作者:董多,讲师;电话:0570-8026634:E-mail:dongduohit@163.com
  • 相关文献

参考文献6

二级参考文献102

共引文献216

同被引文献24

引证文献2

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部 意见反馈