均化矾土基铝镁浇注料的渣蚀行为和机制研究 预览 被引量:2

Slag corrosion and its mechanism of homogenized bauxite based Al203 - MgO castables
在线阅读 下载PDF
收藏 分享 导出
摘要 为了研究均化现土熟料的使用范围,以质量分数为30%的5+ 3 mm、2 0 %的 3 -1 mm、2 0 %的≤1 mm 的均化矾土为骨料,以12%的≤0.074 mm的棕刚玉粉、1 0 %的≤0.074 mm的鎂砂粉、5 % 的≤2 mm的 a - Al20 3 微粉、3%的≤0.088 mm的 Si0 2微粉为基质粉,外加0.2%的减水剂制备了均化矾土基铝镤浇注料,并采用 FactSage?热化学软件建立了熔渣对该浇注料侵蚀的热化学模型,同时通过动态抗渣侵蚀试验研究了其抗渣侵 蚀机制.结果表明:1)渣蚀后接近热面附近的骨料周围会生成较大的裂纹,对试样的抗渣性能产生不利的影响;2)均化矾土基铝鎂浇注料与熔渣反应,反应产物为CA6、复合尖晶石、 C2AS、 CAS2 等;3 )热化学模拟结果表 明,均化矾土骨料与熔渣反应时,表面生成约62.5 pm厚的CA6层,使得其向渣中的溶解为间接溶解,而基质与 炫淹反应时,未生成ca 6层, For the study of application range of homogenized bauxite grogs, homogenized bauxite based Al203-Mg0 castables were prepared using 30% homogenized bauxite (by mass,the same hereinafter,5 - 3 mm) ,20% homogenized bauxite (3 -1 mm) ,and 20% homogenized bauxite ( ≤1 mm) as aggregate, 12% brown fused corundum powder (≤0.074 mm),10% magnesia powder (≤0.074 mm),5% a-AI203 micropowder ( ≤2 nm) ,3% Si02 micropowder ( ≤0.088 mm) as matrix materials,and extra-adding 0.2% water reducer. A thermo-chemical model was developed for the corrosion of homogenized bauxite based Al203-Mg0 castables by molten slag through FactSage? software. The corrosion mechanism was investi-gated through the dynamic testing method. The results show that: (1) large cracks form around the aggre-gates near the hot face after the slag test,which have negative effects on slag resistance; (2) CA6,com- posite spinel,C2AS and CAS2 form when the molten slag reacts with Al203-Mg0 castable; (3 ) the thermo-chemical simulation results indicate that a CA6 layer with thickness about 62.5 nm forms on the surface,re-sulting in indirect dissolution of aggregate into s la g;but no CA6 layer is formed when the matrix reacts with the molten slag,showing direct dissolution of matrix into slag.
作者 王洛 韩兵强 陈庆洁 杨亚东 孔为民 罗琼 李楠 Wang Luo, Han Bingqiang,Chen Qingjie,Yang Yadong,Kong Weimin,Luo Qiong,Li Nan(The State Key Laboratory of Refractories and Metallurgy,Wuhan University of Sci-ence and Technology,Wuhan 430081,Hubei,China)
出处 《耐火材料》 CAS 北大核心 2016年第4期256-260,共5页 Refractories
基金 国家973计划项目(20l4CB660802) 湖北省教育厅资助项目(D20141103).
关键词 铝镁浇注料 均化矾土 感应炉 抗渣性 热化学模拟 alumina-magnesia castables homogenized bauxite induction furnace slag resistance thermo-chemistry simulation
作者简介 王洛:男,1990年生,硕士研究生.E-mail:wangluowk@163.com 通讯作者:韩兵强,男,1973年生,博士,教授.E-mail:hbqref@wust.edu.cn