纳米纤维素晶须/明胶复合膜的制备与结构及性能 预览 被引量:1

Fabrication, Structure and Properties of Cellulose Nanowhiskers/Gelatin Composite Film
在线阅读 下载PDF
分享 导出
摘要 明胶作为一种生物质材料,具有良好的成膜性能、阻氧性能。然而,明胶韧性差,遇水易溶胀等缺点在很大程度上限制其应用。文中以明胶为基体,纤维素晶须(CW)作为分散相,制备纳米纤维素/明胶生物基复合膜。采用透射电镜、扫描电镜、紫外分光光度计、溶胀及力学性能测试研究复合膜的结构与性能。结果表明,当晶须加入量为15%时,复合膜的溶胀度降低为纯明胶膜的1/4,表明纤维素晶须可改善明胶膜在水中的稳定性;当纤维素晶须含量为9%左右,不仅能改善明胶基体韧性,还提高了明胶基体的强度。 Gelatin as a kind of biomass possesses excellent film-forming ability and oxygen barrier property. However, application of gelatin is limited due to its poor toughness and water resistant. In this work, cellulose nanowhiskers/gelatin composite film was fabricated with cellulose whiskers as dispersion phase. The structure and properties of composite film were characterized by TEM, SEM, UV-vis spectroscopy, swelling and mechanical tests. The results indicate that cellulose whiskers improve the mechanical property and stability in water. The swelling ratio of composite film is about 4 folds compared with pure gelatin film when the whiskers content is 15 %. Mechanical property of composite film is improved with 9% whiskers addition.
作者 裴莹 徐高强 李玉辉 郑学晶 刘捷 汤克勇 Ying Pei, Gaoqiang Xu,Yuhui Li, Xuejing Zheng, Jie Liu, Keyong Tang ( College of Materials Science and Engineering, Zhengzhou University, Zhengzhou 450001 , China )
出处 《高分子材料科学与工程》 CSCD 北大核心 2017年第8期45-49,共5页 Polymer Materials Science & Engineering
基金 国家自然科学基金资助项目(U1404509,51473150) 中国博士后科学基金资助(2015M572118) 河南省教育厅项目(15A430044)
关键词 纤维素晶须 明胶 溶胀性能 力学性能 cellulose whiskers gelatin swelling property mechanical property
作者简介 通讯联系人:汤克勇,主要从事天然高分子研究,E-mail:kytangzzu@126.com
  • 相关文献

同被引文献6

引证文献1

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部 意见反馈