微动垫夹持刚度对微动疲劳寿命的影响分析 被引量:1

Analysis on effect of contact pad gripping rigidity on fretting fatigue life
收藏 分享 导出
摘要 以单卡头式微动疲劳试验装置为对象,设计了不同微动垫夹持型式的微动疲劳试验装置,建立了两种试验装置的物理模型,结合理论分析和有限元数值仿真,从微动垫夹持刚度的角度分析了影响微动疲劳寿命的主要因素,并进行了试验对比验证。结果表明:夹持刚度的减小对SWT(Smith-Watson-Topper)微动疲劳损伤参量的最大值及位置影响较小,且使其在接触区域的分布趋于对称,可显著地降低相对滑移幅值,进而减小微动疲劳过程中的磨损程度;与夹持刚度较大的试验装置相比,夹持刚度较小的试验装置测试得到的微动疲劳试验寿命较长。 An apparatus with different contact pad gripping rigidity was designed on the basis of single clamp fretting fatigue apparatus. The mechanical models of two apparatuses were developed. By the investigation of the experimental results and numerical analysis, the effect of contact pad gripping rigidity on fretting fatigue damage was discussed. Results indi- cate that, with the decrease of the contact pad gripping rigidity, the maximum SWT (Smith-Watson-Topper) fatigue parameter value remains almost the same and tends to have a symmetrical distribution over contact interface. As a result, the relative slip amplitude and fretting wear decrease correspondingly; the smaller contact pad gripping rigidity of the appa- ratus means the longer fretting fatigue life.
作者 文长龙 崔海涛 董磊 WEN Changlong, CUI Haitao, DONG Lei (Jiangsu Province Key Laboratory of Aerospace Power System, College of Energy and Power Engineering, Nanjing University of Aeronautics and Astronautics, Nanjing 210016, China)
出处 《航空动力学报》 CSCD 北大核心 2017年第9期2238-2242,共5页 Journal of Aerospace Power
基金 航空科学基金(20151052018)
关键词 微动疲劳 夹持刚度 SWT(Smith-Watson-Topper)损伤参量 相对滑移幅值 疲劳寿命 fretting fatigue gripping rigidity SWT (Smith-Watson-Topper) fatigueparameter relative slip amplitude fatigue life
作者简介 文长龙(1991-),男,硕士生,主要从事结构疲劳研究。
  • 相关文献

参考文献5

二级参考文献118

共引文献8

同被引文献4

引证文献1

投稿分析

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部 意见反馈