乙醇胺溶液中Inconel690合金微动磨损与腐蚀的交互作用 预览 被引量:1

Fretting Corrosion and Wear Interactions of Inconel690 Alloy in Ethanolamine Solution
在线阅读 下载PDF
分享 导出
摘要 采用PLINT微动腐蚀试验机,位移幅值为100~200μm,法向载荷为20~80 N,频率为2 Hz,循环次数为10000次,在乙醇胺(ETA)溶液中对Inconel690合金进行了切向微动腐蚀试验。结果表明:微动腐蚀与磨损呈"负交互作用",其原因是表面膜和腐蚀产物组成的第三体层参与微动磨损过程,改变了摩擦接触界面状态;微动使自腐蚀电位负移,位移幅值增加,引起腐蚀速率增大;Inconel690合金在ETA溶液中的微动磨损机制主要表现为磨粒磨损和剥层的共同作用。 Fretting corrosion test of Inconel690 in ethanolamine(ETA) solution was carried out by PLINT fretting corrosion rig under the conditions of displace amplitudes 100-200 μm,normal loads from 20 N to 80 N,frequency 2 Hz and number of fretting cycles 10 000.The results showed that the reason of the negative interaction between fretting corrosion and wear was that the surface film and corrosive products of the third layer took part in the process of fretting wear.The frictional contact interface states were changed.The self corrosion potential showed a more obvious negative shift during the fretting,and corrosion rate increased with increasing displacement.Abrasive wear and delamination were main fretting wear mechanisms of Inconel690 alloy in ETA solution.
作者 祁学潮 任平弟 张晓宇 徐涛 李长香 QI Xuechao1 , REN Pingdi1, ZHANG XiaoyuI, XU Tao1 , LI Changxiang1(1. Tribology Research Institute, National Key Laboratory of Traction Power, Southwest Jiaotong University, Chengdu 610031, China; 2. Nuclear Power Institute of China, Chengdu 610041, China)
出处 《腐蚀与防护》 北大核心 2017年第11期840-843,866共5页 Corrosion & Protection
基金 国家自然科学基金(51075324 U1534209)
关键词 Inconel690合金 微动腐蚀 腐蚀特性 交互作用 Incone1690 alloy fretting corrosion corrosion characteristic interaction
作者简介 通信作者:任平弟,教授,博士,主要从事摩擦学及表面工程研究工作,028-87603924,rpd@swjtu.edu.cn
  • 相关文献

参考文献5

二级参考文献45

共引文献21

同被引文献5

引证文献1

投稿分析

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部 意见反馈