高延性纤维混凝土材料冻融循环试验研究 预览 被引量:1

Experimental research on freezing and thawing test of high ductile fiber concrete
在线阅读 下载PDF
分享 导出
摘要 采用快速冻融方法对高延性纤维混凝土(HDFC)试件和混凝土试件进行了冻融循环对比试验。观察测定了不同冻融循环次数作用后HDFC与混凝土试件的表观特征及抗压承载力、峰值应变、极限应变、质量损失和动弹性模量,对HDFC与混凝土的抗冻性能进行了对比分析。试验结果表明:冻融循环作用后,HDFC与混凝土相比,抗压承载力和延性高,内部损伤和劣化程度低。 The freezing and thawing test of high ductility fiber concrete(HDFC)specimens and concrete specimens were made by the method of rapid freezing and thawing.The surface characteristics and compressive bearing capacity,peak strain,ultimate strain,mass loss and dynamic elastic modulus of HDFC and concrete specimens after different freezing and thawing cycles were observed and measured.The results showed that after the freezing and thawing cycles the compressive strength and ductility of HDFC were higher than that of concrete,and the internal damage and deterioration of HDFC were lower than that of concrete.
作者 杨步云 寇佳亮 孙静 YANG Buyun, KOU Jialiang, SUN Jing ( School of Civil Engineering and Architecture, Xi'an University of Technology, Xi'an 710048, China)
出处 《混凝土》 北大核心 2017年第11期114-117,121共5页 Concrete
基金 国家自然科学青年基金项目(51278402) 陕西省自然科学基础研究计划项目(14JK1516)
关键词 高延性纤维混凝土 冻融循环 抗冻性能 损伤和劣化 high ductile fiber concrete freezing and thawing cycle frost resistance property damage and deterioration
作者简介 杨步云(1991-)男,在读硕士研究生,研究方向:高延性纤维混凝土材料。