强流脉冲电子束抛光模具钢的研究 预览

Investigation of Polishing Mold Steel by High Current Pulsed Electron Beam
在线阅读 下载PDF
分享 导出
摘要 为探索模具钢表面抛光新工艺,采用强流脉冲电子束(HCPEB)对奥氏体模具钢Cr12Mo V粗糙表面进行辐照处理。通过OM、SEM、XRD分析处理试样表面形貌及结构,采用RM-20表面粗糙度仪、FM-300显微硬度计和摩擦磨损试验机测试试样表面的粗糙度、显微硬度和摩擦系数的变化。结果表明:在较大束流强度作用下,试样表面的山脊形貌、熔坑等各种缺陷得到控制,表面粗糙度降低,结构细化;同时,提高了试样表面的显微硬度,改善了摩擦性能。 In order to explore the new process of mold steel polishing, the rough surface of austenitic mold steel Cr12MoV was irradiated by high current pulsed electron beam (HCPEB). The morphology and structure of the irradiated surface were analyzed by optical microscope (OM), scanning electron microscope (SEM), X-Ray Diffraction (XRD), and the change of roughness,microhardness and friction coefficient of the samples were tested by RM-20 surface roughness tester,FM-300 microhardness tester and friction-wear testing machine. The re- sults showed that the roughness reduces and the structure refines due to controlling all kinds of the defects of the samples, such as ridge morphologies, melting pits, etc. ;at the same time, the microhardness increases and the friction performance improves on the sample surface.
作者 杨君宝 刘高 樊永军 陈梨 YANG Junbao1 ,LIU Gao2 ,FAN Yongjun2 ,CHEN Li2 (1Shenyang Ligong University, Shenyang 110159, China ;2. Chongqing Construction Industry (Group) Limited Liability Company, Chongqing 400054, China)
出处 《沈阳理工大学学报》 CAS 2017年第6期5-9,共5页 Transactions of Shenyang Ligong University
基金 辽宁博士科研启动基金资助项目(20141088)
关键词 强流脉冲电子束 抛光 粗糙度 显微硬度 摩擦系数 模具钢 HCPEB polishing roughness microhardness frictional coefficient mold steel
作者简介 杨君宝(1977-),男,博士,工程师,研究方向:高温合金、材料表面改性等。
  • 相关文献

参考文献3

二级参考文献20

共引文献1

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部 意见反馈