保护气体对06Cr19Ni10钢焊接接头疲劳性能的影响 预览

Effect of different protective atmospheres on fatigue performance of 06Cr19Ni10 stainless steel welded joints
在线阅读 下载PDF
收藏 分享 导出
摘要 O2与CO2作为MAG焊常用的活性气体,其加入量对奥氏体不锈钢接头的疲劳性能有着一定的影响。通过脉动拉伸疲劳试验和金相组织分析,研究06Cr19Ni10铜MAG焊对接接头在两种不同保护气氛下的疲劳性能。结果表明:当保护气体为φ(Ar)95%+φ(c02)5%时,中值疲劳强度为300MPa;当保护气体为φ(Ar)97%+φ(02)3%时,中值疲劳强度为302.5MPa。二者疲劳性能良好且相近。试件断裂位置主要集中在热影响区,启裂区有明显启裂源;扩展区的疲劳纹清晰;终断区为韧窝型韧性断口;两种接头焊缝组织基体均为奥氏体,基体上分布δ铁素体。 The oxygen and carbon dioxide are available active gas and both are commonly applied in MAG welding,the amount of their addition has definite influence on the fatigue performance of austenitic stainless steel. Through pulsating tensile fatigue test and metallographic structure analysis,the fatigue performance of MAG welding butt joint of 06Crl9Nil0 steel with two different kinds of protective atmospheres is studied. The results show that the median fatigue strength of φ(Ar)95%+φ(CO2)5% is 300 MPa,the median fatigue strength of φ(Ar)97%+φ( O2)3% is 302.5 MPa. The fracture location of specimen mainly concentrates in the heat affected zone. The crack starter location is obvious in the crack initiation zone;the fatigue striations on the extending zone are clear; the final broken zone is the toughness dimple type of fracture;the matrixes of the microstructures of two types of welded joints are both austenitic,and there are δ ferrites distribute on the matrix.
作者 宗桓旭 许鸿吉 耿涛 祁艺洋 ZONG Huanxu,XU Hongji, GENG Tao, QI Yiyang (School of Materials Science and Engineering, Dalian Jiaotong University, Dalian 116028, China)
出处 《电焊机》 2018年第1期101-105,共5页 Electric Welding Machine
关键词 06Cr19Ni10不锈钢 MAG焊接头 金相组织 疲劳性能 06Crl 9Ni 10 stainless steel MAG welded joint microstructure fatigue performance
作者简介 宗桓旭(1992-),男,硕士.主要从事轨道交通关键材料焊接的研究。E—mail:m18841123974@163.com。
  • 相关文献

参考文献6

二级参考文献27

共引文献22

投稿分析

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部 意见反馈