多巴胺表面改性反应时间对镀银玻璃微球及导电硅橡胶性能的影响 预览

Effect of Dopamine Surface Modification Time on Properties of Silver Coated Silica Microsphere and Conductive Silicone Rubber
在线阅读 免费下载
分享 导出
摘要 利用聚多巴胺(PDA)优异的黏结性能对镀银玻璃微球(SiO2/Ag)进行表面改性,在不影响导电硅橡胶的导电性的前提下,提高导电硅橡胶的力学性能。结果表面,PDA改性能够提高SiO2/Ag在硅橡胶中的分散性,控制反应时间能够实现PDA层厚度可控,从而实现导电硅橡胶导电性可控。改性反应时间为8h时,SiO2/Ag填充的导电硅橡胶的Payne效应,损耗角正切(tanδ),正硫化时间(T90),静态接触角达到最小,拉伸强度最大,电学性能符合应用标准。 The surface modification of silver coated silica microsphere ( SiO2/Ag) was carried out by using ex- cellent bonding properties of polydopamine (PDA) to improve the mechanical properties of conductive silicone rubber without affecting the conductivity of conductive silicone rubber. The results show that PDA surface modification can improve the dispersion of SiO2/Ag in silicone rubber. By controlling the reaction time, controllable thickness of PDA layer can be achieved so that controlling the conductive silicon rubber conductivity can be achieved. The Payne' s effect, loss angle of tangent ( tanδ), optimum curing time ( T90 ), contact angle and tensile strength of conductive sili- cone rubber filled with modified SiO2/Ag reach the optimum state when the PDA coating time is 8 h and electrical performance meets application standards.
作者 李润源 王建月 王姝瑛 于焕光 侯杰 LI Runyuan ,WANG Jianyue, WANG Shuying ,YU Huanguang ,HOU Jie (Aerospace Research Institute of Materials & Processing Technology, Beijing 100076)
出处 《宇航材料工艺》 CSCD 北大核心 2018年第2期13-19,共7页 Aerospace Materials & Technology
关键词 镀银玻璃微球 多巴胺 表面改性 导电硅橡胶 分散性 Silver coated silica microsphere, Dopamine, Surface modification, Conductive silicone rubber, Dispersibility
作者简介 李润源,1989年出生,硕士,主要从事橡胶加工、硫化工艺的研究。E-mail:lirunyuan2006@163.com
  • 相关文献

参考文献5

二级参考文献40

共引文献27

投稿分析

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部 意见反馈