电子束辐照制备卤胺抗菌棉织物 预览 被引量:1

Preparation of N-halamine antibacterial cotton fabrics via electron beam irradiation
在线阅读 下载PDF
收藏 分享 导出
摘要 选用(3-丙烯酰胺丙基)三甲基氯化铵(AAPTAC)为卤胺抗菌单体,采用共辐照工艺制备抗菌棉织物。研究了吸收剂量对织物含氯量和断裂强力的影响。结果表明,织物含氯量随吸收剂量的增加而增多,织物断裂强力随吸收剂量的增加而下降。傅里叶红外光谱证明AAPTAC已成功接枝到棉织物上,扫描电子显微镜分析表明,棉织物的表面具有覆盖物。吸收剂量为43.3 kGy时,氯化后的棉织物可在5 min内杀灭100%的金黄色葡萄球菌和大肠杆菌。 A Co-irradiation process was employed for antibacterial finishing of cotton fabrics using an N-halamine antiseptic,(3-acrylamidopropyl) trimethylammonium chloride(AAPTAC), as the monomer. The effect of the absorbed dose on the chlorine content and breaking strength were studied. The results showed that the chlorine content and breaking strength of the treated fabrics increased and decreased, respectively, with the increasing absorbed doses. Fourier transform infrared spectroscopy(FTIR) proved that AAPTAC was successfully grafted onto the cotton fiber. Scanning electron microscopy showed that the surfaces of the Co-irradiated process-treated cotton fabrics were covered by layers. When the absorbed dose was 43.3 kGy, the treated cotton fabrics after chlorination could kill 100% of Staphylococcus aureus and Escherichia coli O157:H7 within 5 min of contact time.
作者 马志鹏 丁放 林兴焕 任学宏 MA Zhipeng,DING Fang,LIN Xinghuan,REN Xuehong(Key Laboratory of Eco-textiles, Ministry of Education, Jiangnan University, Wuxi 214122, China)
出处 《辐射研究与辐射工艺学报》 CAS CSCD 2018年第4期31-35,共5页 Journal of Radiation Research and Radiation Processing
基金 江苏省产学研前瞻性联合研究项目(BY2015057-18)资助
关键词 电子束辐照 (3-丙烯酰胺丙基)三甲基氯化铵 棉织物 抗菌整理 Electron beam irradiation (3-Acrylamidopropyl) trimethylammonium chloride Cotton fabrics,Antibacterial finish
作者简介 马志鹏,男,1977年2月出生,2005年于西安工程大学获得硕士学位,目前为江南大学博士研究生,主要从事抗菌纺织品的研究,副教授;通信作者:任学宏,博士,教授,博导,xhren@jiangnan.edu.cn