化学清洗造成的换热器管束失效分析 预览

Analysis of Heat Exchanger Tube Bundle Failure Caused by Chemical Cleaning
在线阅读 下载PDF
分享 导出
摘要 采用金相显微镜、直读光谱仪、X射线衍射仪(XRD)和能谱分析仪等分析方法,对某炼化厂连续重整预加氢换热器E-101D管束钢(0Cr18Ni10Ti)穿孔进行失效分析。分析结果表明:管束的成分及组织均符合设计要求,但其中的夹杂物(氧化钛)使钢的强度、塑性、韧性及抗疲劳性能下降;管束的穿孔是由内外壁同时腐蚀的结果,氯离子是引起不锈钢点蚀的主要原因,而氯离子的来源是停工期间化学清洗所带入的。 Perforation failure analysis was carried out on tube bundle steel(0Cr18Ni10Ti)of pre-hydrogenation heat exchanger E-101 D in continuous catalytic reforming unit by means of metallographic microscope,direct reading spectrometer,X-ray diffraction(XRD)and energy spectrum analyzer.The results showed that tube bundle composition and microstructure met the design requirements,but the performance of steel strength,plasticity,toughness and fatigue resistance was degraded by titanium oxide included in the steel.Tube bundle perforation resulted from simultaneous action of inner and outer wall caused by chloride ion coming from chemical cleaning during shutdown.
作者 徐拥军 呼立红 郑丽群 万晔 XU Yongjun;HU Lihong;ZHENG Liqun;WAN Ye(Shenyang Jianzhu University,Shenyang 110168,China;Shenyang Zkwell Corrosion Control Technology Co. ,Ltd. ,Shenyang 11 0 1 68,China)
出处 《石油化工腐蚀与防护》 CAS 2019年第1期61-64,共4页 Petrochemical Corrosion and Protection
关键词 换热器 穿孔 化学清洗 氯离子 heat exchanger perforation chemical cleaning chloride ion
作者简介 徐拥军(1992-),沈阳建筑大学材料科学与工程专业在读硕士,主要研究方向为石油化工腐蚀与防护。E-mail:990541995@qq.com.
  • 相关文献

参考文献10

二级参考文献73

共引文献82

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部 意见反馈