冷轧原料质量缺陷及改进措施 预览

Quality defect of cold rolled raw material and improvement measure
在线阅读 下载PDF
分享 导出
摘要 冷轧原料质量缺陷主要有钢卷表面氧化铁皮残留,钢卷头部松卷、扁卷,卷取头部宽度拉窄等.采用优化工艺制度,调整开轧轧制时间,降低头部温度,提高设备精度,张力分段控制等措施减少缺陷.出钢温度控制在(1150±10)℃,薄规格轧制时入精轧温度在1020℃左右.轧辊冷却水流量应控制在450.4m^3/h左右.经过试验,产品质量缺陷得到有效改善. The quality defects of cold-rolled raw material mainly include iron oxide residue on surface of steel coil,loose and flat rolls on the head of steel coil,and narrow the width of roll head.Optimized process system is adopted to adjust rolling time,decrease head temperature,improve equipment precision,tension section control and other measures to reduce defects.The temperature of exit steel is controlled at (1 150 ± 10)℃,and the temperature of finish rolling is controlled about 1 020 ℃ when rolling thin specifications.Roller cooling water flow should be controlled about 450.4 m^3 /h.The test show that the quality defect has been improved effectively.
作者 隋跃川 Sui Yuechuan(Benxi Steel Group Corporation,beiying Iron & Steel (Group) Co.,Ltd.,Benxi 117017,China)
出处 《金属制品》 2019年第2期53-56,共4页 Metal Products
关键词 冷轧原料 质量缺陷 抗拉强度 氧化膜 张力控制 cold-rolled raw material quality defects tensile strength oxidation film tension control
作者简介 隋跃川,1990年生,本钢集团北营钢铁(集团)股份有限公司轧钢厂助理工程师。
  • 相关文献
投稿分析

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部 意见反馈