铜合金表面甲基苯并三氮唑-溴化十六烷基吡啶复合钝化膜的制备及耐蚀性研究 预览

Preparation and corrosion resistance of tolyltriazole–cetylpyridinium bromide composite passivation film on copper alloys
在线阅读 下载PDF
分享 导出
摘要 采用含甲基苯并三氮唑(TTA)与溴化十六烷基吡啶(CPB)的钝化液在H62铜合金表面得到TTA-CPB复合钝化膜。通过单因素试验确定了最佳成膜条件为:TTA2.5g/L,CPB0.5g/L,pH5.0,温度75℃,时间16min。所得复合钝化膜均匀、平整,呈光亮的银白色,厚度约为9μm,兼具TTA和CPB的特征官能团,对水的接触角为82.96°,耐中性盐雾腐蚀时间超过48h。 H62 copper alloy was treated in a bath comprising tolyltriazole (TTA) and cetylpyridinium bromide (CPB) to form a TTA–CPB composite passivation film on its surface. The optimal process conditions were determined by single factor experiment as follows: TTA 2.5 g/L, CPB 0.5 g/L, pH 5.0, temperature 75℃, and time 16 min. The composite passivation film is uniform, even, bright, and silvery white with a thickness of ca.9 μm, has the characteristic functional groups of TTA and CPB and a water contact angle of 82.96°, and can endure the neutral salt spray corrosion over 48 hours.
作者 伍荣龙 郭瑞光 WU Rong-long;GUO Rui-guang(Key Lab of Water, Environment and Ecology in North China, MoE, Xi’an University of Architecture and Technology, Xi’an 710055, China)
出处 《电镀与涂饰》 CAS CSCD 北大核心 2019年第9期421-425,共5页 Electroplating & Finishing
基金 国家自然科学基金(20976143) 无锡高新区科技领军人才创业项目(2017年)。
关键词 铜合金 复合钝化 甲基苯并三氮唑 溴化十六烷基吡啶 耐蚀性 疏水性 copper alloy composite passivation tolyltriazole cetylpyridinium bromide corrosion resistance hydrophobicity
作者简介 第一作者:伍荣龙(1993–),男,湖北襄阳人,在读硕士研究生,从事工业污染防护研究;通信作者:郭瑞光(1962–),男,江西赣州人,博士,教授,研究方向为工业污染防护、重金属污染综合防治、水污染控制。