手机摄像模组跌落仿真与优化 预览

Drop simulation and optimization on mobile phone camera module
在线阅读 下载PDF
收藏 分享 导出
摘要 为有效解决智能手机摄像模组滤光片在跌落过程中的脆性开裂问题,开展手机跌落过程的有限元仿真,并对仿真结果进行试验验证。手机正面跌落时,滤光片受力最大,其失效主要是由摄像模组内部镜头撞击镜座导致的。保证手机摄像模组中镜头与镜座之间的距离大于马达载体与马达基体之间的距离,可以有效防止滤光片的失效。研究滤光片热固胶的弹性模量、胶宽和胶厚对滤光片应力的影响,结果表明:改变滤光片热固胶的弹性模量对滤光片的脱落影响较大;滤光片应力随滤光片热固胶胶宽的增加先增大后减小,随滤光片热固胶胶厚的增加而减小。仿真结果可为滤光片热固胶的用法与用量提供指导。 To effectively solve the brittle cracking problem of mobile phone camera module filter in the dropping process,the finite element simulation of mobile phone dropping process is carried out.The simulation results are verified by test.The force of the filter is the maximum when the mobile phone face bumps on the ground.The failure is mainly caused by the impact of the lens inside the camera module on the lens base.If it is ensured that the distance between lens and lens base in mobile phone camera module is larger than that between motor carrier and motor base,the failure of the filter can be effectively prevented.The effects of elastic modulus,width and thickness of filter thermosetting adhesive on the stress of filter are studied.The results show that changing the elastic modulus of filter thermosetting adhesive has a great influence on the shedding of the filter.The filter stress increases first and then decreases with the increase of filter thermosetting adhesive width,and decreases with the increase of filter thermosetting adhesive thickness.The simulation results can provide guidance for the usage and dosage of filter thermosetting adhesive.
作者 王明珠 王忠伟 李凤云 蒋恒 WANG Mingzhu;WANG Zhongwei;LI Fengyun;JIANG Heng(Research and Development Center,Ningbo Sunny Opotech Co.,Ltd.,Ningbo 315400,China)
出处 《计算机辅助工程》 2019年第2期68-73,共6页 Computer Aided Engineering
关键词 手机 摄像模组 跌落 撞击 滤光片 失效 热固胶 可靠性 mobile phone camera module drop impact filter failure thermosetting adhesive reliability
作者简介 王明珠(1978—),女,湖北武汉人,硕士,研究方向为光学技术,(E-mail)wangmz@sunnyoptical.com;通信作者:李凤云(1991-),女,安徽阜阳人,硕士,研究方向为冲击动力学,(E-mail)gdlfy@sunnyoptical.com.
  • 相关文献

参考文献6

二级参考文献101

  • 1谢里阳,林文强.疲劳剩余寿合分布的当量关系及可靠性计算方法[J].东北大学学报:自然科学版,1995,16(6):598-602. 被引量:4
  • 2汤立群,孙晖,何庭蕙,刘逸平,詹克银.跌落条件下手机的冲击动力学分析和结构优化设计[J].现代制造工程,2006(6):112-114. 被引量:7
  • 3于捷,申桂香,贾亚洲.基于三参数威布尔分布的数控机床的可靠性评价[J].现代制造工程,2007(5):18-20. 被引量:17
  • 4Ghidini T, Donne D C. Fatigue life prediction using fracture mechanics methods [ J ]. Engineering Fracture Mechanics, 2009, 76( 1 ) : 134 - 148. 被引量:1
  • 5Sheikh A K, Younas M. A reliability model for fatigue life characterization[ J]. International Journal of Fatigue, 1995, 17(2) : 121 - 128. 被引量:1
  • 6Castillo E, Fernandez Canteli A. A general regression model for lifetime evaluation and prediction [ J ]. International Journal of Fracture, 2001, 107(2) : 117 - 137. 被引量:1
  • 7Liu Y M, Mahadevan S. Probabilistic fatigue life prediction using an equivalent initial flaw size distribution [ J]. International Journal of Fatigue, 2009, 31 (3) : 476 - 487. 被引量:1
  • 8Grell W A, Laz P J. Probabilistic fatigue life prediction using afgrow and accounting for material variability [ J ]. International Journal of Fatigue, 2010, 32 ( 7 ): 1042 - 1049. 被引量:1
  • 9Mohanty J R, Verma B B, Ray P K. Prediction of fatigue crack growth and residual life using an exponential model: Part I ( constant amplitude loading) [ J ]. International Journal of Fatigue, 2009, 31(3) : 418 -424. 被引量:1
  • 10Mohanty J R, Verma B B, Ray P K. Prediction of fatigue crack growth and residual life using an exponential model: Part I1 ( mode - I overload induced retardation) [ J ]. International Joural of Fatigue, 2009, 31 ( 3 ) : 425 - 431. 被引量:1

共引文献37

投稿分析

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部 意见反馈
新型冠状病毒肺炎防控与诊疗专栏