Al-Mn系铝合金箔拉伸试样星点纹路产生的原因分析 预览

Cause Analysis on Star Pattern for Tensile Sample of Al-Mn Aluminum Alloy Foil
在线阅读 免费下载
收藏 分享 导出
摘要 对不同回复退火工艺的Al-Mn系铝合金箔在经过拉伸试验后表面产生的星点纹路进行了对比,并对不同程度的星点纹路进行了EBSD分析。结果表明,星点纹路是因材料经过退火后其旋转立方织构及立方织构比例增加所造成的。铸轧晶粒组织越粗大,退火的温度越高、时间越长,拉伸后的试样表面更易出现星点纹路现象。通过铸轧晶粒组织的细化、退火工艺的调整可避免出现拉伸试样星点纹路的现象。 The degree of the surface star pattern of the Al-Mn aluminum alloy foil after tensile test using different recovery annealing processes was compared, and the star pattern of different degrees was analyzed by EBSD. The results show that the star pattern is caused by the increase of the proportion of rotating cube texture and the proportion of cube texture after annealing. The larger the continuous casting and rolling grain size, the higher the temperature and the longer the time of annealing, the surface of sample are prone to star pattern after stretching. By refining the grain structure and adjusting the annealing process, the star pattern of the tensile test can be avoided.
作者 池国明 胡展奎 CHI Guo-ming;HU Zhan-kui(Ruyuan Dongyangguang UACJ Fine Aluminum Foil Co.,Ltd., Shaoguan 512721, China)
出处 《铝加工》 CAS 2019年第4期13-18,共6页 Aluminium Fabrication
基金 广东省省级科技计划项目(2015B090926007).
关键词 Al-Mn系铝合金箔 星点纹路 铸轧组织 回复退火 织构 Al-Mn aluminum alloy foil star pattern continuous casting and rolling microstructure recovery annealing texture
作者简介 池国明(1969-),男,河北石家庄人,大学本科,教授级高级工程师.
  • 相关文献

参考文献3

二级参考文献44

共引文献20

投稿分析

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部 意见反馈
新型冠状病毒肺炎防控与诊疗专栏