电解锰渣制备高掺量免烧胶凝陶粒的抗压强度研究 认领

Study on the Compressive Strength of High-volume Non-sintering Cementitious Ceramsite Prepared from Electrolytic Manganese Slag
在线阅读 下载PDF
收藏 分享 导出
摘要 以电解锰渣为高掺量添加剂,探究电解锰渣添加量、水泥添加量、粉煤灰添加量、及激发剂石灰添加量对陶粒抗压强度的影响。结果表明:电解锰渣添加量为58.7%,粉煤灰添加量为29.3%,水泥添加量为12%,激发剂为NaOH添加量占电解锰渣、水泥、粉煤灰总质量的8%时,陶粒抗压强度最大为7.0 MPa。 Using electrolytic manganese slag as a high-volume additive, explore the influence of electrolytic manganese slag addition, cement addition, fly ash addition, and activator lime addition on the compressive strength of ceramsite. The results show that the addition amount of electrolytic manganese slag is 58.7 %, the addition amount of fly ash is 29.3 %, the addition amount of cement is 12 %, and the activator is NaOH when the addition amount is 8 % of the total mass of electrolysis manganese slag, cement and fly ash. The maximum compressive strength of ceramsite is 7.0 MPa.
作者 段瑶瑶 陈晓亮 黄薇 黄透敏 陈群 杨林 王海峰 Duan Yaoyao;Chen Xiaoliang;Huang Wei;Huang Toumin;Chen Qun;Yang Lin;Wang Haifeng(College of Materials and Metallurgy,Guizhou University,Guiyang 550025;Guizhou Provincial Key Laboratory of Metallurgical Engineering and Energy Saving,Guiyang 550025;Research Technology Center of Manganese Materials for Battery of Guizhou Province,Tongren 554300,China)
出处 《广东化工》 CAS 2020年第17期27-28,11,共3页 Guangdong Chemical Industry
基金 国家大创项目(201810657001) 国家自然科学基金(51764006、51864012) 贵州省科学合作计划项目([2019]1411、[2017]5788、[2018]5781、[2016]5302、[2019]2841)。
关键词 抗压强度 免烧陶粒 无害化处理 激发 compressive strength non-fired ceramsite harmless treatment excitation
  • 相关文献

参考文献11

二级参考文献102

共引文献157

202103读书月活动
维普数据出版直通车
今日学术
投稿分析
职称考试

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部 意见反馈