TiO2载体制备条件及结构对MnOx/TiO2催化剂性能的影响 预览

Effects of TiO2 Preparation Condition and Structure on the Performance of MnOx/TiO2 Catalysts
在线阅读 下载PDF
分享 导出
摘要 采用水热法一步反应制备锐钛矿结构TiO2晶体,通过浸渍法负载活性组分MnOx得到MnOx/TiO2低温脱硝催化剂。利用X射线衍射仪(XRD)、比表面积分析仪(BET)、扫描电子显微镜(SEM)和透射电子显微镜(TEM)等手段,研究制备过程中水热温度、水热时间以及硫酸钠用量对TiO2载体和MnOx/TiO2催化剂性能的影响。结果表明,水热温度为120℃,水热时间为22 h以及硫酸钠与尿素摩尔比为0.12的条件下,得到的TiO2结晶度高,分散性好,最大比表面积为234.54 m2·g-1。由其制备的MnOx/TiO2低温脱硝催化剂具有最佳的低温脱硝活性,在空速为20000 h-1,反应温度为200℃时,催化剂脱硝率可达90%以上。 Anatase TiO2 crystals were synthesized by one-pot hydrothermal reaction,and were used as carriers to prepare low-temperature denitrification catalysts MnOx/TiO2 by impregnation method.The effects of hydrothermal temperature,hydrothermal time and dosage of sodium sulfate on the performances of TiO2 carriers and MnOx/TiO2 catalysts were investigated by XRD,BET,SEM and TEM.The results show that when the hydrothermal temperature is 120℃,the hydrothermal time is 22 h and the molar ratio of sodium sulfate to urea is 0.12,the obtained TiO2 carriers have high crystallinity,excellent dispersion properties and maximum specific surface area which is up to 234.54 m2·g-1.Moreover,under this conditions,the MnOx/TiO2 catalyst has the best low-temperature catalytic activity,when the reaction temperature is 200℃and the space velocity is 20000 h-1,the NO conversion can up to 90%.
作者 王其波 谢峻林 刘小青 李凤祥 公丕军 何峰 WANG Qi-bo;XIE Jun-lin;LIU Xiao-qing;LI Feng-xiang;GONG Pi-jun;HE Feng(State Key Laboratory of Silicate Materials for Architectures,Wuhan University of Technology,Wuhan 430070,China)
出处 《硅酸盐通报》 CAS 北大核心 2019年第3期711-716,721共7页 Bulletin of the Chinese Ceramic Society
基金 国家重点研发计划专项(2017YFB0304304).
关键词 低温脱硝催化剂 催化剂载体 水热法 二氧化钛 low-temperature SCR catalyst catalyst carrier hydrothermal method titanium dioxide