高吸水性树脂的合成与性质研究 预览 被引量:3

Synthesis and properties of corn starch graft to acrylic acid/acrylamide
在线阅读 下载PDF
收藏 分享 导出
摘要 采用水溶液法以(NH4)2S2O8为引发剂,以玉米淀粉、丙烯酸(AAC)、丙烯酸胺(AAM)为原料,对淀粉在80~85 ℃糊化15~30 min,引发剂与淀粉质量比为0.4%~0.6%,单体与淀粉质量比为4~6,AAC与AAM质量比为2.0~2.5,聚合温度为50~60 ℃,反应2~3 h条件下合成了玉米淀粉接枝AAC/AAM吸水树脂,其吸水率为400~700 g*g-1,对0.9%的NaCl溶液吸液率为100~150 g*g-1,实验结果表明,该树脂的耐盐性明显提高. By means of aqueous polymerization,the superabsorbent resin had been synthesized with corn starch,acrylic acid(AAC) and acrylamide(AAM) as raw materials, and using (NH4)2S2O8 as an initiator. The optimum conditions are paste temperature 80~85 ℃,paste time 15~30 minutes,initiator/starch mass ratio 0.4%~0.6%, monomer/starch mass ratio 4~6,AAC/AAM mass ratio 2.0~2.5, reaction temperature 50~55 ℃, reaction time 2~3 h.As a result, the absorptive capacity of the superabsorbent resin is 400~700 g·g-1 for water and 100~150 g·g-1 for 0.9% NaCl solution,this shows that the saltresistance property of the resin was improved obviously.
作者 李雅丽 曹会兰 杨建武 LI Yali1, CAO Huilan1, YANG Jianwu2 (1.Dept. Chem., Weinan Teachers College, Weinan 714000,Shaanxi,China;2.Appl. Chem. Inst.,Northwest Univ., Xi'an 710069,Shaanxi,China)
出处 《宝鸡文理学院学报:自然科学版》 CAS 2003年第2期 121-123,共3页 Journal of Baoji University of Arts and Sciences(Natural Science Edition)
基金 陕西省教育厅资助项目
关键词 玉米淀粉 丙烯酸 丙烯酰胺 接枝共聚 高吸水性树脂 水溶液法 corn starch acrylic acid acrylamide graft copolymerization