国产和进口Ni36夹杂物对比分析研究 预览
1
作者 姚雷 陆建生 《宝钢技术》 CAS 2019年第1期24-28,共5页
用电解萃取和夹杂物定量统计分析工具,对国产和进口Ni36的夹杂物情况进行研究。为更好地表征夹杂物,得出更具统计性的结果,同时降低试验时间,采用两套不同的参数设置来分别研究小尺寸夹杂物和大尺寸夹杂物。研究结果显示,对于大尺寸夹杂... 用电解萃取和夹杂物定量统计分析工具,对国产和进口Ni36的夹杂物情况进行研究。为更好地表征夹杂物,得出更具统计性的结果,同时降低试验时间,采用两套不同的参数设置来分别研究小尺寸夹杂物和大尺寸夹杂物。研究结果显示,对于大尺寸夹杂物,在数量、种类、尺寸和形态上,二者不存在明显的差异;对于小尺寸夹杂物,从数量和种类上,二者存在明显的差异,进口产品夹杂物的数量明显大于国产的,且在种类分布中,进口Ni36更加偏向于与MgO相关的夹杂物。 展开更多
关键词 夹杂物 定量表征 Ni36 MGO
在线阅读 下载PDF
Fluid Inclusion and H-O Isotope Geochemistry of the Phapon Gold Deposit, NW Laos: Implications for Fluid Source and Ore Genesis
2
作者 Linnan Guo Shusheng Liu +6 位作者 Lin Hou Jieting Wang Meifeng Shi Qiming Zhang Fei Nie Yongfei Yang Zhimin Peng 《地球科学学刊:英文版》 SCIE CAS CSCD 2019年第1期80-94,共15页
The Phapon gold deposit, located in northern Laos, is a unique large-scale gold deposit in Luang Prabang-Loei metallogenic belt. It is hosted in the Lower Permian limestone and controlled by a NE-trending ductile-brit... The Phapon gold deposit, located in northern Laos, is a unique large-scale gold deposit in Luang Prabang-Loei metallogenic belt. It is hosted in the Lower Permian limestone and controlled by a NE-trending ductile-brittle fault system. There are three types of primary ore including auriferous calcite vein type, disseminated type, and breccia type, and the first two are important in the Phapon gold deposit. Based on fluid inclusion petrography and microthermometry, three types of primary fluid inclusions including type 1 liquid-rich aqueous, type 2 vapor-rich aqueous and type 3 daughter mineralbearing aqueous were identified in hydrothermal calcite grains. The ore-forming fluids are normally homogeneous, as indicated by the widespread type 1 inclusions with identical composition. The coexistence of type 1 and type 2 inclusions, showing similar final homogenization temperature but different compositions, indicate that fluid immiscibility did locally take place in both two types of ores. The results of microthermometry and H-O isotopes geochemistry indicate that there are little differences on ore-fluid geochemistry between the auriferous calcite vein-type and disseminated type ores. The oreforming fluids are characterized by medium-low temperatures(157–268 oC) and low salinity(1.6 wt.%–9.9 wt.% NaCl eq.). It is likely to have a metamorphic-dominant mixed source, which could be associated with dehydration and decarbonisation of Lower Permian limestone and Middle–Upper Triassic sandstones during the dynamic metamorphism. The fluid-wallrock interaction played a major role, and the locally occurred fluid-immiscible processes played a subordinate role in gold precipitation. Combined with the regional and ore deposit geology, and ore-fluid geochemistry, we suggest that the Phapon gold deposit is best considered to be a member of the epizonal orogenic deposit class. 展开更多
关键词 FLUID inclusion H-O isotopes FLUID SOURCE ore genesis Phapon gold deposit northern Laos
弹簧钢62Si2MnA带钢边部翘皮缺陷分析与改进 预览
3
作者 李军 《金属制品》 2019年第1期35-38,共4页
全程跟踪带钢加工过程,结合扫描电镜检验和金相显微分析方法,分析弹簧钢原料冷轧加工过程中,在带钢表面靠近边部的位置产生翘皮缺陷的原因,判断出缺陷产生在冷轧环节,造成该缺陷的原因是轧辊温度过高使润滑剂失效,轧辊和带钢粘连,带钢... 全程跟踪带钢加工过程,结合扫描电镜检验和金相显微分析方法,分析弹簧钢原料冷轧加工过程中,在带钢表面靠近边部的位置产生翘皮缺陷的原因,判断出缺陷产生在冷轧环节,造成该缺陷的原因是轧辊温度过高使润滑剂失效,轧辊和带钢粘连,带钢在脱离轧辊后粘结部位发生撕裂。在滴油轧制改为乳化液轧制方式后,缺陷情况得到明显改善。 展开更多
关键词 62Si2MnA 扫描电镜 金相分析 夹杂物 冷轧
在线阅读 下载PDF
模铸不锈钢冶炼过程中夹杂物的来源分析
4
作者 张跃良 陈根保 +3 位作者 史茜 丁斌华 朱光宇 黄崇德 《云南冶金》 2019年第1期83-87,共5页
不锈钢中大型夹杂物( >1.5级)严重影响不锈钢的力学及加工性能,对于电炉(EAF)、氩氧精炼炉(AOD)、钢包精炼炉(LF)冶炼工艺,通过现场大生产实验及分析,冶炼过程中大型夹杂物的来源主要有三大来源:深脱氧过程中加入铝而形成的氧化铝,AO... 不锈钢中大型夹杂物( >1.5级)严重影响不锈钢的力学及加工性能,对于电炉(EAF)、氩氧精炼炉(AOD)、钢包精炼炉(LF)冶炼工艺,通过现场大生产实验及分析,冶炼过程中大型夹杂物的来源主要有三大来源:深脱氧过程中加入铝而形成的氧化铝,AOD炉渣的卷入,AOD炉衬的侵蚀。 展开更多
关键词 不锈钢 夹杂物 AOD LF炉
在线阅读 免费下载
下行波磁场在熔体净化中的应用 预览
5
作者 张林英 杨勋刚 +1 位作者 姚志勇 胡旭峰 《科技创新与应用》 2019年第3期178-179,共2页
研究了在0Hz~50Hz范围下行波磁场作用下,圆柱型坩埚内铀金属熔体中的夹杂物运动迁移行为。模拟与实验结果表明,在下行波磁场作用下,熔体中夹杂物在圆柱型坩埚上部靠近磁场发生器处,具有明显的富集区域,下行波磁场对熔体中夹杂物具有净... 研究了在0Hz~50Hz范围下行波磁场作用下,圆柱型坩埚内铀金属熔体中的夹杂物运动迁移行为。模拟与实验结果表明,在下行波磁场作用下,熔体中夹杂物在圆柱型坩埚上部靠近磁场发生器处,具有明显的富集区域,下行波磁场对熔体中夹杂物具有净化作用。 展开更多
关键词 下行波磁场 熔体净化 夹杂物
在线阅读 下载PDF
河钢宣钢72A热轧帘线钢质量提升实践 预览
6
作者 闫卫兵 张丽峰 冯旻昱 《河北冶金》 2019年第2期55-58,19共5页
河钢宣钢为进一步提高72A产品质量,与国内某先进生产厂(以下简称M厂)产品进行了全面对比,通过分析钢的化学成分、气体含量、夹杂物尺寸以及组织和性能的差异,有针对性地制定改进措施,使产品质量得到显著提升,满足国内某知名加工企业(以... 河钢宣钢为进一步提高72A产品质量,与国内某先进生产厂(以下简称M厂)产品进行了全面对比,通过分析钢的化学成分、气体含量、夹杂物尺寸以及组织和性能的差异,有针对性地制定改进措施,使产品质量得到显著提升,满足国内某知名加工企业(以下简称N企业)要求。 展开更多
关键词 72A 帘线钢 质量提升 夹杂 组织性能
在线阅读 下载PDF
含烧结镁橄榄石中间包涂料对汽车板钢洁净度的影响
7
作者 郁书中 王德军 +1 位作者 刘正龙 邓承继 《炼钢》 CAS 北大核心 2019年第1期39-46,共8页
研究了汽车板钢样品分别与镁质中间包涂料和添加了质量分数20%烧结镁橄榄石的镁质中间包涂料在1 600℃和氩气气氛保护下,作用1 h或2 h后对钢液成分及钢中TC,T. O,TN,TS含量及钢中夹杂物成分和尺寸的影响。结果表明:钢样在添加烧结镁橄... 研究了汽车板钢样品分别与镁质中间包涂料和添加了质量分数20%烧结镁橄榄石的镁质中间包涂料在1 600℃和氩气气氛保护下,作用1 h或2 h后对钢液成分及钢中TC,T. O,TN,TS含量及钢中夹杂物成分和尺寸的影响。结果表明:钢样在添加烧结镁橄榄石颗粒涂料的坩埚中冶炼后,钢中Si含量降低,P和Al含量均增加,Mn含量变化不显著;T. O含量在与坩埚样作用1 h后略有增加,但随着作用时间延长至2 h钢中T. O含量明显降低;而纯镁质中间包涂料中冶炼钢样的T. O含量变化相反。两组钢样中TN、TS含量均增加。钢中的夹杂物尺寸在与中间包涂料作用后有所增加,夹杂物的成分从原始钢样中较为单一的Al2O3、MnO以及TiOx等夹杂变化为(P,Si) O-MnS以及CaO-Mn(O,S)-(Al,Si) O等复合氧化物夹杂。 展开更多
关键词 中间包 烧结镁橄榄石 洁净钢 夹杂物
大线能量焊接用钢CGHAZ冲击韧性内在机理分析
8
作者 邹宗园 韩舒婷 +1 位作者 李银潇 王超 《中国冶金》 CAS 北大核心 2019年第1期18-24,共7页
针状铁素体(AF)一直被认为是提升大线能量焊接用钢粗晶热影响区(CGHAZ)韧性最有效的组织之一,但在一些试验中,有时即使发现CGHAZ中有大量AF组织,韧性也并不好。为了研究大线能量焊接用钢CGHAZ中不同类型组织及夹杂物对其冲击韧性的影响... 针状铁素体(AF)一直被认为是提升大线能量焊接用钢粗晶热影响区(CGHAZ)韧性最有效的组织之一,但在一些试验中,有时即使发现CGHAZ中有大量AF组织,韧性也并不好。为了研究大线能量焊接用钢CGHAZ中不同类型组织及夹杂物对其冲击韧性的影响作用,从CGHAZ冲击试验出发,借鉴前人研究经验,对影响CGHAZ韧性的主要因素进行深入分析。结果显示,CGHAZ中微米级夹杂物容易成为裂纹萌生点,而晶内位错效应、冲击触发的体积效应等可以抑制裂纹传播,CGHAZ中析出的少量纳米级碳氮化物可以提升AF形核能力,增强CGHAZ韧性和强度,但当析出粒子过多时,会降低CGHAZ韧性。 展开更多
关键词 CGHAZ 铁素体 冲击韧性 裂纹 夹杂物
无取向硅钢RH精炼过程中夹杂物行为研究 预览
9
作者 陈天颖 刘静 +2 位作者 程朝阳 骆忠汉 毕云杰 《武汉科技大学学报:自然科学版》 CAS 北大核心 2019年第1期1-7,共7页
针对无取向硅钢RH精炼工艺各阶段现场取样,系统研究了钢中夹杂物数量、尺寸及成分的演变规律及钢水的洁净度变化。结果表明,钢中夹杂物主要是Al2O3及其复合夹杂,尺寸大部分集中在0~2μm,形状以球形和椭球形为主。从RH进站到RH出站,钢中... 针对无取向硅钢RH精炼工艺各阶段现场取样,系统研究了钢中夹杂物数量、尺寸及成分的演变规律及钢水的洁净度变化。结果表明,钢中夹杂物主要是Al2O3及其复合夹杂,尺寸大部分集中在0~2μm,形状以球形和椭球形为主。从RH进站到RH出站,钢中夹杂物数量不断减少,共减少了9.63个/mm^2,而尺寸小于1μm的夹杂物仅仅减少了0.85个/mm^2,可见细小夹杂物去除效果不明显。加Al脱氧一个循环时,夹杂物体积百分数下降最快,平均去除率为71.6%,钢中平均总氧含量下降了70%,钢液的洁净度明显提高。但铝脱氧后生成大量细小夹杂物,且随着加Al循环的进行有明显长大的趋势。适当延长铝脱氧的净循环时间,可能是促进细小夹杂物充分长大去除的有效途径。 展开更多
关键词 无取向硅钢 RH精炼 夹杂物 铝脱氧 总氧含量
在线阅读 下载PDF
GCr18Mo轴承钢采用铝及稀土金属脱氧的研究 预览
10
作者 苏新 郭曙强 +3 位作者 乔梦然 秦礼彬 郑红妍 任忠鸣 《上海金属》 CAS 北大核心 2019年第1期88-93,共6页
以GCr18Mo轴承钢为研究对象,采用铝脱氧和稀土金属脱氧两种方式降低钢中的氧含量,并观察脱氧后钢中夹杂物的形貌和分布。首先通过热力学计算,分别采用一阶和二阶活度相互作用系数得到1873K熔炼温度下的铝-氧平衡曲线。然后通过铝脱氧试... 以GCr18Mo轴承钢为研究对象,采用铝脱氧和稀土金属脱氧两种方式降低钢中的氧含量,并观察脱氧后钢中夹杂物的形貌和分布。首先通过热力学计算,分别采用一阶和二阶活度相互作用系数得到1873K熔炼温度下的铝-氧平衡曲线。然后通过铝脱氧试验验证理论曲线的合理性。发现采用一阶相互作用系数的结果更贴近试验数据。并采用稀土金属镧、铈、钇作为脱氧剂与铝对比,发现脱氧能力顺序是镧>铈>钇>铝。最后对比夹杂物的大小和分布,发现铝脱氧的含铝夹杂物形态多样,大小各异;稀土金属脱氧后的含稀土夹杂物多为白色圆点状,尺寸一般为2~5μm。 展开更多
关键词 GCr18Mo轴承钢 稀土 热力学 脱氧平衡 夹杂物
在线阅读 下载PDF
天津市学前自闭症儿童融合教育现状调查 预览
11
作者 潘柏均 孙丹妮 江帆 《教育教学论坛》 2019年第5期50-52,共3页
目前,天津市学前自闭症儿童融合教育处于初步探索阶段,为了解其发展现状,本研究通过对幼儿园教师的问卷调查,融合自闭症儿童的实地观察,融合幼儿园教师的访谈,研究发现幼儿园教师对融合教育的认同度有待提高,融合教育模式不成熟,融合幼... 目前,天津市学前自闭症儿童融合教育处于初步探索阶段,为了解其发展现状,本研究通过对幼儿园教师的问卷调查,融合自闭症儿童的实地观察,融合幼儿园教师的访谈,研究发现幼儿园教师对融合教育的认同度有待提高,融合教育模式不成熟,融合幼儿园缺乏师资、资金、家长的支持。对此应提高幼儿园教师对融合教育的认同度、相关科研组织加强对学前自闭症儿童融合教育的研究、政府制定相关政策支持、引入资金保障。 展开更多
关键词 天津市 学前自闭症儿童 融合教育
在线阅读 下载PDF
中碳珠光体型高速车轮钢的韧化机理
12
作者 周世同 李昭东 +3 位作者 潘涛 左越 杨才福 雍岐龙 《钢铁》 CAS CSCD 北大核心 2019年第2期75-82,共8页
韧性是影响高速车轮运行安全的关键性能指标。为了阐明中碳珠光体型高速车轮钢的韧化机理,对夹杂物改性和组织韧化两方面进行了深入研究。研究结果表明,硫化物包裹氧化物的夹杂物改性提高了车轮钢的韧性。车轮钢中的氧化物夹杂容易在夹... 韧性是影响高速车轮运行安全的关键性能指标。为了阐明中碳珠光体型高速车轮钢的韧化机理,对夹杂物改性和组织韧化两方面进行了深入研究。研究结果表明,硫化物包裹氧化物的夹杂物改性提高了车轮钢的韧性。车轮钢中的氧化物夹杂容易在夹杂物与基体界面处产生裂纹,并向周围基体扩展;当氧化物被硫化物包裹后,裂纹仅在夹杂物本身产生,保护了周围基体。在w(Mn)=0.75%的成分体系下,当硫的质量分数提高到0.006%及以上时,硫化物在固相线温度以上析出,可以实现对氧化物的较好包裹,改善车轮钢的韧性;硫化物在车轮热加工过程中会发生回溶与再析出,破坏复合夹杂物的包裹效果,提高硫质量分数或降低热加工温度,可以提高复合夹杂物的热稳定性。奥氏体晶粒尺寸和先共析铁素体体积分数是车轮钢组织韧化的关键控制因素。细化奥氏体晶粒尺寸、提高铁素体体积分数,断口中解理面尺寸减小,韧性撕裂区增多。 展开更多
关键词 车轮钢 韧性 夹杂物 组织
Comparison between the surface defects caused by Al2O3 and TiN inclusions in interstitial-free steel auto sheets 预览
13
作者 Rui Wang Yan-ping Bao +2 位作者 Zhi-jie Yan Da-zhao Li Yan Kang 《矿物冶金与材料学报:英文版》 SCIE EI CAS CSCD 2019年第2期178-185,共8页
Al2O3 and TiN inclusions in interstitial-free(IF)steel deteriorate the properties of the steel.To decrease the defects of cold-rolled sheet,it is important to clearly distinguish between the degrees of damage caused b... Al2O3 and TiN inclusions in interstitial-free(IF)steel deteriorate the properties of the steel.To decrease the defects of cold-rolled sheet,it is important to clearly distinguish between the degrees of damage caused by these two inclusions on the surface quality of the steel.In this study,a nanoindenter was used to test the mechanical properties of the inclusions,and the distribution and size of the inclusions were obtained by scanning electron microscopy(SEM).It was found that when only mechanical properties are considered,TiN inclusions are more likely to cause defects than Al2O3 inclusions of the same size during the rolling process.However,Al2O3 inclusions are generally more inclined to cause defects in the rolling process than TiN inclusions because of their distribution characteristic in the thickness direction.The precipitation of Al2O3 and TiN was obtained through thermodynamical calculations.The growth laws of inclusions at different cooling rates were calculated by solidification and segregation models.The results show that the precipitation regularity is closely related to the distribution law of the inclusions in IF slabs along the thickness direction. 展开更多
关键词 interstitial-free steel INCLUSIONS nanoindenter INCLUSION PRECIPITATION
在线阅读 下载PDF
Silymarin-laden PVP-PEG polymeric composite for enhanced aqueous solubility and dissolution rate: Preparation and in vitro characterization 预览
14
作者 Abid Mehmood Yousaf Usman Rashid Malik +2 位作者 Yasser Shahzad Tariq Mahmood Talib Hussain 《药物分析学报:英文版》 CAS CSCD 2019年第1期34-39,共6页
The aim of this work was to develop, optimize and characterize a silymarin-laden polyvinylpyrrolidone (PVP)-polyethylene glycol (PEG) polymeric composite to resolve low aqueous solubility and dissolution rate problem ... The aim of this work was to develop, optimize and characterize a silymarin-laden polyvinylpyrrolidone (PVP)-polyethylene glycol (PEG) polymeric composite to resolve low aqueous solubility and dissolution rate problem of the drug. A number of silymarin-laden polymeric formulations were fabricated with different quantities of PVP K-30 and PEG 6000 by the solvent-evaporation method. The effect of PVP K-30 and PEG 6000 on the aqueous solubility and dissolution rate was investigated. The optimized formulation and its constituents were characterized using powder X-ray diffraction (PXRD), differential scanning calorimetry (DSC), scanning electron microscopy (SEM) and Fourier transform infrared spectroscopy (FTIR) techniques. Both the PEG 6000 and PVP K-30 positively affected the aqueous solubility and dissolution rate of the drug. In particular, a formulation consisting of silymarin, PVP K-30 and PEG 6000 (0.25/1.5/1.5, w/w/w) furnished the highest solubility (24.3972.95 mg/mL) and an excellent dissolution profile (-100% in 40 min). The solubility enhancement with this formulation was -1150-fold as compared to plain silymarin powder. Moreover, all the constituents existed in the amorphous state in this silymarin-laden PVP-PEG polymeric composite. Accordingly, this formulation might be a promising tool to administer silymarin with an enhanced effect via the oral route. 展开更多
关键词 SILYMARIN HYDROPHILIC polymers Inclusion Solid dispersion Aqueous solubility DISSOLUTION rate
在线阅读 下载PDF
金刚线基线用钢丝标准化研究 预览
15
作者 王宝玉 闵学刚 +1 位作者 郑川川 沈献民 《金属制品》 2019年第1期56-58,共3页
介绍金刚线基线用钢丝标准研究的意义,对金刚线基线用钢丝标准制定原则及其原料提出要求;重点研究基线的性能特征,如基线规格、公称直径及允许偏差、椭圆度、破断拉力与扭转值及抗拉强度名义值,工艺性能参数如圈径、翘距的量化指标,给... 介绍金刚线基线用钢丝标准研究的意义,对金刚线基线用钢丝标准制定原则及其原料提出要求;重点研究基线的性能特征,如基线规格、公称直径及允许偏差、椭圆度、破断拉力与扭转值及抗拉强度名义值,工艺性能参数如圈径、翘距的量化指标,给出钢丝工艺性能试验方法。 展开更多
关键词 金刚线 夹杂物 标准化 破断拉力 翘距
在线阅读 下载PDF
浅析精炼炉渣碱度对钢液夹杂物的影响 预览
16
作者 董亚楠 《宽厚板》 2019年第1期39-42,共4页
舞钢在生产钢锭成材130 mm以上厚度、有国标探伤要求的钢板时,因夹杂物去除不彻底导致探伤合格率偏低。通过对比不同LF精炼终渣碱度以及不同VD真空处理后软吹时间状态下的钢液夹杂物数量,分析影响钢液夹杂物含量的主要因素。结果表明:... 舞钢在生产钢锭成材130 mm以上厚度、有国标探伤要求的钢板时,因夹杂物去除不彻底导致探伤合格率偏低。通过对比不同LF精炼终渣碱度以及不同VD真空处理后软吹时间状态下的钢液夹杂物数量,分析影响钢液夹杂物含量的主要因素。结果表明:合理的精炼炉渣碱度和真空处理后软吹时间有利于去除钢液中夹杂物,可有效减少钢锭成材厚板的夹杂物数量,提高国标探伤要求钢板的探伤合格率。 展开更多
关键词 夹杂物 模铸 精炼炉渣碱度 软吹时间
在线阅读 下载PDF
高级别船板钢生产过程中夹杂物的演变规律
17
作者 周宇涛 杨树峰 +1 位作者 李京社 梁雪 《钢铁》 CAS CSCD 北大核心 2019年第1期33-42,共10页
通过采用扫描电镜对船板钢F40中的夹杂物进行全流程系统分析,研究了冶炼过程中夹杂物的形成和演变规律,并采用夹杂物的弹性模量概念对其在轧制过程中的变形机理进行解释。结果表明,LF出站后钢中的主要夹杂物为MgO-Al2O3复合夹杂,在钙处... 通过采用扫描电镜对船板钢F40中的夹杂物进行全流程系统分析,研究了冶炼过程中夹杂物的形成和演变规律,并采用夹杂物的弹性模量概念对其在轧制过程中的变形机理进行解释。结果表明,LF出站后钢中的主要夹杂物为MgO-Al2O3复合夹杂,在钙处理后夹杂物逐渐向低熔点的CaO-Al2O3-MgO-CaS系夹杂转变。在轧制过程中,高弹性模量的夹杂物,在轧制中相对塑性变形低。热力学计算表明,当船板钢中的w([Als])为0.02%~0.04%时,为使夹杂物改性完全,钙处理后钢液中的w([Ca])应控制在0.001 8%~0.002 8%。为避免钙处理后生成CaS,可通过控制w([S])在0.002 1%以内,减小其对浇注过程和钢性能的不利影响。 展开更多
关键词 船板钢 夹杂物 钙处理 钙铝酸盐 轧制
49MnVS非调质钢水口堵塞原因分析
18
作者 曾志崎 杨乾坤 +3 位作者 艾克南 谢剑波 李健 付建勋 《钢铁》 CAS CSCD 北大核心 2019年第1期43-48,70共7页
非调质钢中含有较多的铝和硫,常在连铸过程中因水口蓄积钙铝酸盐或硫化钙而发生堵塞,影响生产的顺利进行。为了探究非调质钢的水口堵塞原因并提出预防措施,采用X射线荧光分析、X射线衍射分析和热力学计算,分析了非调质钢49MnVS的水口堵... 非调质钢中含有较多的铝和硫,常在连铸过程中因水口蓄积钙铝酸盐或硫化钙而发生堵塞,影响生产的顺利进行。为了探究非调质钢的水口堵塞原因并提出预防措施,采用X射线荧光分析、X射线衍射分析和热力学计算,分析了非调质钢49MnVS的水口堵塞结瘤物。结果表明,水口堵塞物主要由CaO·6Al2O3、CaO·Al2O3、MgO·Al2O3和金属铁相组成,生产中钙的收得率仅为预期的53.33%;热力学计算表明,水口堵塞的原因是钢液中的钙铝质量比较低,生成了大量高熔点的CaO·6Al2O3和CaO·Al2O3夹杂物,夹杂物在水口处黏附聚集;同时,由于MgO-C质水口耐火材料被侵蚀,MgO在絮流区与Al2O3碰撞生成MgO·Al2O3,铁液滴在夹杂物孔隙中凝固黏结,使堵塞物进一步长大,将水口完全堵塞。因此,可以通过优化喂线操作、控制钢中的钙铝比位于0.127~0.225、改进水口材质等措施来预防水口堵塞。 展开更多
关键词 非调质钢 夹杂物 钙处理 水口堵塞 热力学计算
Genesis of the Huoshenmiao Mo deposit in the Luanchuan ore district, China: Constraints from geochronology, ?uid inclusion, and H-O-Sisotopes 预览
19
作者 Sai Wang Bing Li +4 位作者 Xingkang Zhang Peng Wang Weiwei Chao Huishou Ye Yongqiang Yang 《地学前缘:英文版》 CAS CSCD 2019年第1期331-349,共19页
The Huoshenmiao deposit is Mo skarn deposit,located in the western part of the Luanchuan ore district.Mineralization process can be divided into a skarn and a quartz-sulfide episodes with six stages:prograde(Ⅰ),retro... The Huoshenmiao deposit is Mo skarn deposit,located in the western part of the Luanchuan ore district.Mineralization process can be divided into a skarn and a quartz-sulfide episodes with six stages:prograde(Ⅰ),retrograde(Ⅱ),quartz-K-feldspar(Ⅲ),quartz-molybdenite(Ⅳ),quartz-pyrite(Ⅴ),and quartzcalcite(Ⅵ).A combined study of geochronology,fluid inclusion(FI),and stable isotopes was conducted to constrain the mineralization age,source of ore materials,as well as the origin and evolution of the ore-forming fluids.Molybdenite Re-Os dating indicates that the deposit was formed in the Late Jurassic(-145 Ma).Theδ^34S values of sulfides range from 3.0‰to 7.1‰,implying that the ore materials in the deposit are magmatic in origin.Three types and six subtypes of FIs are distinguished,namely,aqueous two-phase(W1-and W2-type),daughter mineral-bearing multiphase(S1-and S2-type),and CO2-bearing three-phase(C1-and C2-type).In stagesⅠandⅡ,the W1-type FIs display homogenization temperatures(Th)from 496℃to>600℃,with salinities of 14.9-18.3 wt.%NaCl eqv.The FIs in stagesⅢ,Ⅳand early stageⅤcomposed of coeval S-,C-and W-types,respectively homogenize at similar Th,suggesting the occurrence of boiling.The W1-type FIs in late stageⅤand stageⅥ,yield Th of 102-406℃and salinities of 0-4.7 wt.%NaCl eqv.TheδDH2O andδ^18OH2O values of the ore-forming fluids in quartz-sulfide episode vary from 112‰to-76‰,and 11.0‰to 1.0‰,respectively.All these above observations reveal that the early ore-forming fluids are magmatic in origin,and characterized by high temperature and moderate to high salinity,and gradually evolve to low temperature,low salinity meteoric water.The Huoshenmiao Mo deposit is associated with the magmatism event induced by the protracted subduction of the Izanagi plate beneath the eastern China continent.The decrease in temperature,salinity and f(O2),as well as change of pH due to boiling and fluid-rock interaction,are the main factors controlling Mo deposition. 展开更多
关键词 Molybdenite Re-Os age Fluid INCLUSION H-O-S isotopes Huoshenmiao MO DEPOSIT Luanchuan ORE DISTRICT
在线阅读 下载PDF
钇基稀土钢中间包水口结瘤机理研究 预览
20
作者 温禄 赖朝彬 +3 位作者 罗迪强 王学林 孙乐飞 操瑞宏 《江西冶金》 2019年第1期10-14,33共6页
针对某钢厂生产E36稀土处理钢时水口结瘤的问题,分析了水口结瘤物结构和成分变化.检测结果表明水口结瘤物主要由稀土铝酸盐、稀土硅酸盐及金属相组成,通过分析稀土在钢液中发生的反应,其生成物熔点基本在1 800℃以上,夹杂物颗粒逐渐析出... 针对某钢厂生产E36稀土处理钢时水口结瘤的问题,分析了水口结瘤物结构和成分变化.检测结果表明水口结瘤物主要由稀土铝酸盐、稀土硅酸盐及金属相组成,通过分析稀土在钢液中发生的反应,其生成物熔点基本在1 800℃以上,夹杂物颗粒逐渐析出.因此,结瘤机理可以表述为,稀土与钢液中SiO2、Al2O3等进行反应,并且在流经水口时,与水口耐材发生反应,夹杂物颗粒沉积在水口壁上,经高温烧结后,聚集增大;附着在水口壁上的夹杂物在粘附力的作用下能够克服钢液流动带来的阻力,可以通过提高钢液温度,减少钢液中Al2O3含量,来降低稀土处理钢的水口结瘤. 展开更多
关键词 稀土钢 水口结瘤 夹杂物 连铸
在线阅读 下载PDF