Migration and transformation behavior of heavy metal elements during the calcination process of copper slag
在线阅读 下载PDF
收藏 分享 导出
摘要 为研究铜冶炼渣资源化综合利用过程中,采用煅烧处理工艺时所产生的二次污染,选用FactSage7.0热化学数据库和铜渣成分分析结果模拟计算了体系升温过程中有害重金属元素Zn、Cu、Pb的迁移转化规律。结果表明,100~1200℃区间内,Zn元素全部以固相ZnFe2O4形式存在;温度达到1300℃时,体系中开始释放0.03%的微量气态金属Zn。500~1000℃区间内,Cu元素由固相CuO完全转化为固相(CuO)(Fe2O3),随后在高温区(1100~1300℃)完全进入液相熔融相,并始终以液相(CuO)(Fe2O3)形式存在。Pb元素由固相(PbO)(TiO2)逐渐向气相转变,且在1000℃时完全进入气相,主要含铅气态产物为PbO。 To investigate the secondary pollutant characteristics during the calcination process for the comprehensive utilization of copper slag resources,the components of copper slag were measured,and the migration and transformation of harmful heavy metal(Zn,Cu,Pb)in the heating process were calculated by FactSage 7.0 thermochemical software.The results show that all Zn exists as solid ZnFe2O4 at temperatures from 100~1200℃.At 1300℃,a small amount of gaseous Zn(0.03%)start to form.Cu is transformed from the solid phase CuO to solid phase(CuO)(Fe2O3)in the 500~1000℃.All Cu-containing species is converted into liquid phase(CuO)(Fe2O3)from 1100~1300℃.Pb is gradually transformed from the solid phase(PbO)(TiO2)to gas phase.At 1000℃,all Pb is transferred into gas phase.The Pb-containing gas phase products mainly exists as PbO.
作者 蒋明 孙鑫 何永美 李博 湛方栋 李天国 宁平 JIANG Ming;SUN Xin;HE Yong-mei;LI Bo;ZHAN Fang-dong;LI Tian-guo;NING Ping(College of Resources and Environment,Yunnan Agricultural University,Kunming 650201,China;Faculty ofEnvironmental Science and Engineering,Kunming University of Science and Technology,Kunming 650500,China)
出处 《应用化工》 CAS CSCD 北大核心 2020年第7期1702-1705,共4页 Applied Chemical Industry
基金 国家重点研发计划(2018YFC1900305) 国家自然科学基金(51768074,51708266,41701362)。
关键词 铜渣 煅烧 重金属 转化 copper slag calcination heavy metal transformation